- Our lab tests of HydroArmor® show this material is extremely durable under even the worst service conditions.
- Several days at 250°F (121°C) and immersion in acidic and caustic solutions did not affect dried coats of this material.
- Coats did not lose adhesion or crack when test panels were bent at -30°F (-34°C).
- After weeks of exterior exposure cycling, the HydroArmor® coatings remained intact and there was no adhesion loss.
- HydroArmor® products dry quickly at ambient temperatures.
- HydroArmor® is as safe to use and as easy to clean up as latex house paint.
- HydroArmor® 7720 provides better protection than any of the competitive prodects we’ve tested while avoiding the environmental and safety problems inherent in many such coatings.
Applications & Uses
- Markets
- Applications
- Application Area
- Application Method
- Compatible Substrates & Surfaces
- Application Instructions
- As with any coating, mix product thoroughly before use. All loose dirt and dust should be removed from the surface to be coated before application.
- HydroArmor® 7720 is normally applied to all floor surfaces and edges and to wall edges with a roller or brush.
- HydroArmor® resists water wash-off after air drying 30 minutes at 45% - 55% relative humidity.
- If not baked, it dries through in 24 hours or less (drying is slowed by high humidity and poor air circulation).
- Until HydroArmor ® dries, overspray can be removed and equipment can be cleaned with water. Dried material can be removed with methyl ethyl ketone.
Properties
- Color (Properties)
- Typical Properties
Value Units Test Method / Conditions Specific Gravity 1.19 - 1.25 - - Solid Content 41 - 45 % - VOC Content 80 - 90 g/L - pH 9 - 10 - - - Technical Properties
Property Value Freeze/Thaw Stability: ASTM D 2243;
4 cycles to -29°C (-20°F)Pass
Sprayable after hand mixing
Technical Details & Test Data
- Test Data
The following tests were performed on panels coated with 8 wet mils of material after drying 21 days, at 20°C (68°F), and 50% RH Effects of Heat Aging:
ASTM C 792; 14 days at 70°C(158°F)Flexibility maintained
No cracks
No loss of adhesionEffects of Exterior Exposure:
GMTM 9505P: Cycle ENo cracks
No loss of adhesion after two weeks of cyclingHumidity Resistance:
ASTM D 2247
Blistering rated by ASTM D 714
Adhesion rated by ASTM D 3359No blistering or softening of film
No loss of adhesion
10 (scale 1 to 10; 10 = best)
5B (scale 1 to 5; 5 = best)Water Resistance Efficiency
ASTM D 540196.7% efficiency Flammability:
MVSS 302Pass
Self-extinguishing within 1”Flammability:
MVSS 302Pass
Self-extinguishing within 1”