Enhanced TDS
Identification & Functionality
- Chemical Family
- Technologies
Features & Benefits
- Labeling Claims
- Ready-to-Use Product Features
- Features & Benefits
- No solvents, plasticizers, or low volatile components
- 1:1 mix ratio by volume, designed for easy use with automated dispense systems
- Excellent moisture penetration seal
- Extreme environmental and abrasion resistance
- Room temperature curing, no heat required
- Non-conductive, non-corrosive
- Outstanding chemical resistance
- High impact strength
- Will not induce stress cracking in polycarbonate or polyethylene parts
- Great balance between high strength and flexibility
- Excellent for bonding plastics
- Excellent for polyamide and nylon bonding
- Very fast setting version available
Applications & Uses
- Markets
- Compatible Substrates & Surfaces
- General Instructions
Surfaces to be bonded must be clean, dry and free from grease, oil, wax, weak oxide films and other contaminants. Bring both components to room temperature prior to mixing. Measure out specified amounts of parts A and B and mix, without introducing bubbles, until homogenous. Meter-mix equipment equipped with an automatic purge is recommended for higher volume applications. Contact your H.B. Fuller representative for suggested application equipment to suit your specific needs. We recommend that containers be purged with nitrogen after they are opened to the air and not all the material is used.
Properties
- Color
- Physical Form
- Component A
- Component B
- Typical Properties
- Cured Properties
- Uncured Properties
| Value | Units | Test Method / Conditions | |
| Viscosity | 1500000.0 | cP | - |
| Value | Units | Test Method / Conditions | |
| Viscosity | 25000.0 | cP | - |
| Value | Units | Test Method / Conditions | |
| Open Time | 15.0 | min | - |
| Value | Units | Test Method / Conditions | |
| Hardness | 80.0 | - | ASTM D2240, Shore D |
| Tensile Strength (at 25°C, 50% RH) | 12.8 | MPa | ASTM D638 |
| Elongation at Break (at 25°C, 50% RH) | 60.0 | % | ASTM D638 |
| Overlap Shear Strength (Aluminum, abraded, at 25°C, 50% RH) | 3765.0 | psi | ASTM D1002 |
| Overlap Shear Strength (Stainless steel, Abraded, 50% RH) | 20.36 | MPa | ASTM D1002 |
| Overlap Shear Strength (E-Coat steel, IPA wipe, 50% RH) | 24.16 | MPa | ASTM D1002 |
| Overlap Shear Strength (Polycarbonate, 20% glass fill, abraded, 50% RH) | 18.38 | MPa | ASTM D1002 |
| Overlap Shear Strength (Nylon 6-6, abraded, 50% RH) | 7.0 | MPa | ASTM D1002 |
| Value | Units | Test Method / Conditions | |
| Specific Gravity | 1.25 | - | - |
| Volume Mix Ratio | 1:1 | - | - |
| Gel Time (at 23°C, 100 gram) | 15.0 | min | - |
| Full Cure (at 23°C) | 2 - 3 | days | - |
| Full Cure (at 70°C) | 1 - 2 | h | - |
Regulatory & Compliance
- Specifications
MIS 31867 Rev. G
Packaging & Availability
- Regional Availability
Storage & Handling
- Shelf Life
- 12 Months
- Storage
Product should be stored in a cool dry place out of direct sunlight. The shelf life is from date of manufacture. Shelf life is based on the products being stored properly at temperatures between 16°C and 25°C. Exposure to temperatures above 25°C will reduce the shelf life. This product should not be frozen. Purge opened containers with dry nitrogen inert blanketing gas before resealing.