H.B. Fuller MP54110 is a two-part unfilled epoxy adhesive designed for bonding of metals, ceramics, and most plastics. This product gives good resistance to water, salt spray, inorganic acids and bases, and most organic solvents. This product has better water and temperature resistance than standard 5-minute epoxy. It was specially formulated to a 1:1 mix ratio for use in either MMD equipment or side-by-side dual cartridges for easy dispensing. A handling cure is normally achieved at room temperature within 30 - 60 minutes, with full cure in 24 hours. An elevated temperature cure schedule can be used to reach final properties quickly.

Chemical FamilyEpoxy & Epoxy Derivatives

Product Type2K (2 component) Adhesive, Epoxy Adhesive, Reactive Adhesive, Structural Adhesive

Compatible Substrates & SurfacesCeramic, Metal, Plastics

FeaturesExcellent Salt Spray Resistance, Free Flowing, Good Adhesion, Good Mechanical Properties, Good Sagging Resistance, Good Toughness, Room Temperature Curing, Solvent Resistance

Technical Data Sheet

Enhanced TDS

Identification & Functionality

Features & Benefits

Applications & Uses

Markets
Compatible Substrates & Surfaces
General Instructions
  • Surfaces to be bonded must be clean, dry and free of other contaminants.
  • Bring both components to room temperature prior to mixing.
  • Measure out specified amounts of parts A and B and stir (without introducing bubbles) until homogenous or use a static mixing nozzle.
  • Apply the uniform mixture to both surfaces.
  • Allow to cure while being held in place with light clamping.

Properties

Physical Form
Appearance
Clear liquid
Component A
ValueUnitsTest Method / Conditions
Viscosity12000.0cP
Component B
ValueUnitsTest Method / Conditions
Viscosity20000.0cP
Cured Properties
ValueUnitsTest Method / Conditions
Hardness80.0ASTM D2240
Overlap Shear Strength (Aluminum, acid etched at 25°C, at 50% RH)15.9MPaASTM D1002
Operating Temperature- 40 - 130°C
Uncured Properties
ValueUnitsTest Method / Conditions
Specific Gravity (Part A)1.17
Specific Gravity (Part B)1.15
Specific Gravity (Mix)1.16
Volume Mix Ratio1:1
Weight Mix Ratio1:1
Pot Life (20 gram)8 - 12min
Handling Time Full Cure (at 23°C)30 - 60min
Handling Time Full Cure (at 66°C)24.0h
Rheological Properties
ValueUnitsTest Method / Conditions
Viscosity (Mixed)15.0cP

Packaging & Availability

Regional Availability
  • Latin America
  • North America

Storage & Handling

Shelf Life
12 Months
Storage Conditions
  • Product should be stored in a cool and dry place out of direct sunlight.
  • The shelf life is from date of manufacture.
  • Shelf life is based on the products being stored properly at temperatures between 12°C and 25°C.
  • Exposure to temperatures above 25°C will reduce the shelf life.
  • This product should not be frozen.