Enhanced TDS
Identification & Functionality
- Chemical Family
- Product Type
- Technologies
Features & Benefits
- Ready-to-Use Product Features
- Features and Benefits
- Cures rapidly at room temperature
- Excellent adhesion and flexible
- Structural bonding of plastic and metal components such as display, top case
Applications & Uses
- Applications
- Application Area
- Application Instructions
1. Bonding surface area should be clean and free of any fluxes, residues, dust or any other contaminants.
2. Use gloves to minimize skin contact.
3. Application to the substrates should be made as soon as possible. Larger quantities and / or higher temperatures will reduce the working time.
4. Keep assembled parts from moving during cure. The bond should be allowed to develop full strength before subjecting to any service load.
5. Remove uncured adhesive
Properties
- Color
- Physical Form
- Cured Properties
- Uncured Properties
Value | Units | Test Method / Conditions | |
Elongation | 48.9 | % | — |
Tensile Strength (at Break) | 13.1 | MPa | — |
Young's Modulus | 430.0 | MPa | — |
Storage Modulus | 1100.0 | MPa | — |
Lap Shear Strength (Aluminum - Aluminum) | 29.8 | MPa | — |
Lap Shear Strength (Polycarbonate - Polycarbonate) | 9.2 | MPa | — |
Lap-Shear Strength (Polycarbonate - Aluminum) | 8.8 | MPa | — |
Lap-Shear Strength (SUS - SUS) | 27.1 | MPa | — |
Value | Units | Test Method / Conditions | |
Viscosity (Part A) | 19000.0 | cP | — |
Specific Gravity (Part A) | 0.99 | g/cm³ | — |
Viscosity (Part B) | 23000.0 | cP | — |
Specific Gravity (Part B) | 1.12 | g/cm³ | — |
Mix Ratio (Part A:Part B, by volume) | 10:1 | — | — |
Work Time | 2 - 4 | min | — |
Fixture Time | 4 - 6 | min | — |
Technical Details & Test Data
- Curing Profile
Recommended cure:
- 24 hours @ 25°C
Packaging & Availability
- Regional Availability
Storage & Handling
- Shelf Life
- 9 Months
- Storage Conditions
FH7026 is supplied in 50ml and 490ml / dual- cartridge. It should be stored in 2℃ to 8℃ in the unopened container in a dry location.
Shelf life is 9 months from date of manufacture.