Enhanced TDS
Identification & Functionality
- Chemical Family
- Product Type
- Technologies
Features & Benefits
- Labeling Claims
- Product Benefits
- Grab-and-go, color-coded caps
- Liquid and gel formulas
- Cures fast at room temperature
- Superior bond strength
- Soft squeeze bottles for easy application
- Controlled dispensing tips mean less waste
- Pin nozzle caps prevent clogs and increase shelf life
- Product Features
High-Performance MRO Solutions
Proactive maintenance can help prevent costly unplanned downtime. It’s a challenge keeping up with maintenance activities while keeping teams trained, equipment operating, and driving productivity. With a full complement of maintenance adhesives, repair epoxies, lubricants, and sealants, GorillaPro adhesives, sealants and lubricants, can repair and improve the reliability of almost any piece of equipment or machinery.- Product Attributes
- Universal: Suitable for general-purpose applications on metals, rubbers, or plastics
- Safe: Tested to ISO 10993-5, making it suitable for use in medical device applications
Applications & Uses
- Applications
- Application Area
- Compatible Substrates & Surfaces
- Cure Method
- Application Instruction
Surfaces to be bonded should be clean and dry. Dispense a drop or drops to one surface only. Apply only enough to leave a thin film layer after compression. Press parts together and hold firmly for a few seconds. Good contact is essential. An adequate bond develops in less that one minute and maximum strength is attained in 24 hours. Wipe off excess adhesive from the top of the container and recap. Products, if left uncapped, may deteriorate by contamination from moisture in the air. Because products cure by polymerization, whitening may appear on the surface of the container or the bonded materials. This will not affect adhesive performance.
Curing Performance
Ambient surface moisture initiates the curing process. Handling strength is reached in a short time, and will vary based on environmental conditions, bond line gap, and other factors. Product will continue to cure for at least 24 hours before full strength and solvent resistance is developed.
Properties
- Physical Form
- Physical Properties
- Cured Properties
- Uncured Properties
| Value | Units | Test Method / Conditions | |
| Technology/Base | Modified Ethyl | — | — |
| Type of Product | Cyanoacrylate | — | — |
| Components | One Component | — | — |
| Curing | Humidity | — | — |
| Consistency | Liquid | — | — |
| Viscosity (at 25°C) | 90 - 130 | cPs | Brookfield SC4-27 |
| Specific Gravity | 1.06 | — | — |
| Value | Units | Test Method / Conditions | |
| Full Cure Time | 24.0 | hours | — |
| Cure Appearance | Clear | — | — |
| Service Temperature | -55 to 95 | °C | — |
| Value | Units | Test Method / Conditions | |
| Flash Point | 80.0 | °C | — |
| Set Time Steel | max. 30 | sec | — |
| Set Time ABS | max. 20 | sec | — |
| Set Time EPDM | max. 20 | sec | — |
Regulatory & Compliance
Technical Details & Test Data
- Test Data
Hot Strength
%RT Strength, Tested at Temperature
Heating Aging
Aged at Temperature Indicated & Tested at 22°C
Time Until Full Cure
%RT Strength
Performance Range By Substrate
N/mm2
Substrate N/mm2 PSI Steel 13.8 to 20.1 2000 to 2920 Rubber* 4.3 to 15.2 630 to 2200 AL 12.6 to 15.8 1830 to 2290 PC#* 17.9 to 22.9 2590 to 3320 PVC** 14.2 to 23.4 2065 to 3400 ABS** 15.1 to 16.4 2185 to 2375 *Rubber figures given are typical. Your results may vary by specific rubber type.
**Tested to ASTM 4501 ***n/r = not recommended- Solvent Resistance
Solvent Resistance Alcohol Excellent Ester (aromatic) Excellent Ketone (aromatic) Poor Aliphatic hydrocarbon (alkanes) Good Aromatic hydrocarbons Good Halogenated hydrocarbons Poor Weak aqueous acid Excellent (Poor if concentrated)
Weak aqueous base Excellent (Poor if concentrated)
Storage & Handling
- Shelf Life
- 12 months
- Storage Condition
Containers should be stored in a cool, dry, dark area. Storage temperature 15.5°C - 25°C (60°F - 77°F), without exposure to direct light or heat. Do not refrigerate.