Features & Benefits
- Labeling Claims
- Ready-to-Use Product Features
- Features and Benefits
- Fast curing system significantly increasing productivity.
- Provides reduced weight by 30% delivering mechanical properties of standard density sealants
- Excellent thermal performance
- Excellent elastomeric properties and strength retention after prolonged exposure to jet fuel, aviation gasoline, hydraulic fluids, oils and lubricants
- Less than 1% linear shrinkage
- Low VOC, eco-friendly sealant which reduces hazardous impact during installation Outstanding adhesion to multiple metals, composites, primers and coatings used in modern aircrafts
Applications & Uses
- Markets
- Applications
- Application Area
- Application Method
- Compatible Substrates & Surfaces
- Cure Method
- Segment
- Application Instructions
- Clean the surface of substrates with appropriated cleaning solutions per specification(s) using an OEM approved lintfree cloth to remove, dirt, grease and processing oils just before the application of sealant. Pour solvent onto cloth to avoid contamination of solvent supply. Clean in small areas at a time. Wipe immediately after application to prevent redeposition of contaminants on the surface. Repeat at least three times or more if required. Use fresh wiping cloth every time! Substrate composition and surface characteristics can greatly vary, which can affect sealant adhesion. It is recommended to determine adhesion characteristics of specific substrates prior to application of sealant to get consistency.
Properties
- Physical Form
- Appearance
- Black Extrudable
- Uncured Properties
Value Units Test Method / Conditions Non Volatile Content min. 96 % - Specific Gravity (Mixed) approx. 1.15 g/cc - Weight Loss 3.65 % AMS2629 Type I Ultimate Elongation (in 42 days, at 140°F) 300 % AMS2629 Tensile Strength (standard cure, in 14 days, at 77°F) 300 psi - Service Temperature (continuous) (-)54 to 250 °F - Low Temperature Flexibility (no loss of adhesion or cracking) -65 °F - Service Temperature (intermittent exposure) max. 360 °F - Ultimate Hardness 52 A - Shore A Viscosity (Part A, Hardener) max. 3,000 poise Viscosity (Part B, Base) 14000 - 16000 poise Viscosity (Mixed) 14,000 – 16,000 poise Mix Ratio (Part A, Hardener) 7.55 vol% Mix Ratio(Part A, Hardener) 12 wt% Mix Ratio (Part B, Base) 100 vol% Mix Ratio (Part B, Base) 100 wt% - Cure Properties
Work Life B-1/2 B-2 Application Life (hrs) ½ 2 Tack free time (hrs) max. 5 max. 8 Cure time to 35 A Durometer (hrs) max. 7 max. 10
Regulatory & Compliance
- OEM Specifications
Packaging & Availability
- Regional Availability
Storage & Handling
- Shelf Life
- 9 months (below 80°F), 30 days (below -40°F)
- Storage Information
The shelf life of WS-8032S Class B is 9 months from the date of manufacturing when stored below 80°F (27°C) in the original unopened container.
The storage life of premixed and frozen material (PMF) is a minimum of 60 days at temperatures below -40°F (- 40°C).