Enhanced TDS
Identification & Functionality
- Chemical Family
- Product Type
- Technologies
Features & Benefits
- Labeling Claims
- Ready-to-Use Product Features
- Product Highlights
- AT-804030 is a 1:1, meter-mix, methacrylate-based structural adhesive formulated to bond engineered thermoplastics,thermosets, composites, and metal structural elements in any combination.
- It has excellent adhesion to as-received metalsurfaces, including aluminum, galvanized, stainless and plated steels.
- It exceeds the strength of PVC, ABS, acrylic,polycarbonate, fiberglass and many other composites and engineering plastics.
- It forms tough, high-strength bonds withoutsurface preparation, primers, or chemical wipes.
- It features a 3-4 minute open time for fast fixturing.
- This product is formulated asa non-sag, high viscosity product with a special filler for holding anchoring studs and clips to walls and ceilings and is easilydispensed from cartridges with static mixer tubes. AT-804030 also provides low temperature impact and peel strength.
- This formulation is Reach Compliant and acid free.
- Substrate : Almost all substrates (except low energy & rubber)
- Non-slide General Purpose Bonder 30 ml cartridge. Seal cap included.
Applications & Uses
- Compatible Substrates & Surfaces
Properties
- Mechanical Properties
- Uncured Properties
- Typical Cured Properties
- Chemical Resistance
- AT-804030 exhibits good resistance to commonly encountered service environments and chemicals.
- Resistance to specific chemicals and environments must be tested by the end-user to ensure theadhesive is compatible to both the substrate and the environment.
| Value | Units | Test Method / Conditions | |
| Peel Strength (Steel, at 0.432 mm Gap) | 11.4 | N/mm | ASTM D 1876 |
| Impact Strength (Aluminum, 2 kg Hammer) | 9.6 | KJ/m² | GM9751P |
| Tensile Shear (Steel, After 24 Hours Cure) | 22.0 | N/mm² | ASTM D1002 |
| Tensile Shear (Aluminum, After 24 Hours Cure) | 22.4 | N/mm² | ASTM D1002 |
| Tensile Shear (Galvanized, After 24 Hours Cure) | 15.2 | N/mm² | ASTM D1002 |
| Tensile Shear (Steel, After 1 Hours Cure (Approx 75% full cure)) | 16.6 | N/mm² | ASTM D1002 |
| Tensile Shear (Aluminum, After 1 Hours Cure (Approx 75% full cure)) | 16.7 | N/mm² | ASTM D1002 |
| Tensile Shear (Galvanized, After 1 Hours Cure (Approx 75% full cure)) | 12.4 | N/mm² | ASTM D1002 |
| Value | Units | Test Method / Conditions | |
| Brookfield Viscosity (Part A, TD at 2.5 rpm) | 250000.0 | cPs | - |
| Brookfield Viscosity (Part B, TD at 2.5 rpm) | 350000.0 | cPs | - |
| Brookfield Viscosity (Part A, TD at 20 rpm) | 50000.0 | cPs | - |
| Brookfield Viscosity (Part B, TD at 20 rpm) | 90000.0 | cPs | - |
| Density (Part A) | 8.82 | pounds/gallon | - |
| Density (Part B) | 8.45 | pounds/gallon | - |
| Mix Ratio | 1:1 | Weight & Volume | - |
| Flashpoint | 11.0 | °C | - |
| Value | Units | Test Method / Conditions | |
| Hardness (Shore D) | 68 - 70 | - | - |
| Elongation | 10.0 | % | - |
| Operating Temperature | - 40 to 125 | °C | - |
| Brookfield Viscosity (Mixed, TD at 2.5 rpm) | 265000.0 | cPs | - |
| Brookfield Viscosity (Mixed, TD at 20 rpm) | 65000.0 | cPs | - |
| Density (Mixed) | 8.63 | pounds/gallon | - |
| Working Time | 3 - 4 | Minutes | - |
| Fixture Time (3 kg weight, Aluminum/ Aluminum) | 5 - 6 | Minutes | - |
| Peak Exotherm Temperature (Range) | 125 to 135 | °C | - |
| Peak Exotherm Time (Range) | 12 - 14 | Minutes | - |
Regulatory & Compliance
- Certifications & Compliance
Packaging & Availability
- Packaging Information
AT-804030 is available in 30 ml.
Storage & Handling
- Shelf Life
- 6 months (in original sealed bulk containers), 12 months (in cartridges)
- Storage Conditions
- The materials can be used with conventional meter/mix dispenseequipment.
- All materials should be stored in a cool place when not used for an extended period of time.
- Do not freeze.