Enhanced TDS
Identification & Functionality
- Product Type
- Technologies
Features & Benefits
Applications & Uses
- Markets
- Application Area
- Cure Method
- Curing Conditions
Cure speed will vary with temperature, relative humidity, depth of material and presence of moisture. Some applications may require special surface preparation. At 21 -25°C, 45 - 55% relative humidity, typical cure depth is 2mm in 24 hours. Requires more time to cure in colder or lower humidity conditions.
- General Instructions
- For best performance bond surfaces should be clean, dry and free of any contaminants and oils.
- Apply a continuous and even bead of silicone to one surface.
- Assemble parts immediately. Remove excess material at once.
Properties
- Physical Form
- Appearance
- Black
- Electrical Properties
- Technical Data
- Cured Properties
- Damp Heat Aging Test Properties
- Uncured Properties
Value | Units | Test Method / Conditions | |
Volume Resistivity | 1.0 x 10¹⁵ | Ω.cm | IEC60093, GB/T1692 |
Breakdown Voltage | 20.0 | kV/mm | IEC 60243-1, GB/T1695 |
Value | Units | Test Method / Conditions | |
Specific Gravity | 1.37 | - | - |
Value | Units | Test Method / Conditions | |
Elongation at Break | 300.0 | % | ISO37, GB/528 |
Lap Joint Shear Strength (Aluminum) | 1.8 | MPa | ISO4587, GB7124 |
Hardness | 48.0 | - | ISO7619, GB/T531, Shore A |
Tensile Strength | 2.3 | MPa | ISO37, GB/528 |
Thermal Service Range | - 54 - 210 | °C | - |
Value | Units | Test Method / Conditions | |
Tensile Strength (at 85°C, 85%RH, 1000h) | 1.6 | MPa | ISO37, GB/528 |
Elongation at Break (85ºC, 85% RH for 1000h) | 320.0 | % | ISO37, GB/528 |
Value | Units | Test Method / Conditions | |
Tack Free Time | 6.0 | min | - |
Full Cure Time (21 - 25°C, 45 - 55% RH, min. 2mm) | 24.0 | h | - |
Regulatory & Compliance
- Certifications & Compliance
Packaging & Availability
- Regional Availability
- Packaging Information
- 310ml
- 400ml
- 600ml
- 25kg
- 235kg
Storage & Handling
- Shelf Life
- 12 Months
- Storage Condition
Product shall be ideally store in a cool, dry area in unopened containers. Material should be stored at a temperature of 8 - 25°C.