Enhanced TDS
Identification & Functionality
- Chemical Family
- Technologies
Features & Benefits
- Ready-to-Use Product Features
- Features
- Higher stability
- Permanent elasticity for thermal expansion and contraction
- Faster cure for manufacturing flexibility
- Good resistant to humidity and weathering
- Excellent resistant to temperatures from (-40°F) up to (250°F)
Applications & Uses
- Applications
- Application Area
- Application Method
- Compatible Substrates & Surfaces
- Cure Method
- Processing
Processing
Consistency
Non-sagging Pasty Surface requirements
Dry Clean free of grease Surface cleaning
Körasolv GL Körasolv PU Körasolv WL Adhesion promoter (absorbing surface) Körabond HG 74 E
Adhesion promoter (non absorbing surface) Körabond HG 81
Product overpaintability after skin formation (depending on paint)
Cleaning
Cleaner for tools
Körasolv GL Körasolv PU Hints
Resistance against UV radiation Not suitable for glass bonding with permanent UV radiation to the bonding area.
Stress cracking Preliminary tests must be carried out on plastics with a tendency to stress cracking. (PMMA, ABS, PC or PS)
Compatibility with polystyrene foams Not suitable for bonding polystyrene foams.
Avoid contact with isocyanate reactive substances Avoid direct contact with isocyanate reactive substances, especially alcohol such as spirit, dilutions, cleaning compounds and fission products of silane-modified polymers or silicones until the adhesive has attained full cure. This will prevent the adhesive from curing properly.
- Low temperatures can cause a temporary increase in viscosity resulting in reduced extrusion and slower curing rates.
- Cleaning: Clean tools immediately after use. Once cured, the material can only be removed mechanically. Appropriate cleaners are listed in the product properties table.
- Dimensioning: The required thickness of the adhesive layer depends on the expected maximum strength and joint movement. We recommend a minimum layer thickness of 2 mm.
Properties
- Physical Form
- Physical Properties
- Cured Properties
- Processing Parameters
- Recommended Operating Conditions
| Value | Units | Test Method / Conditions | |
| Density | 1.2 | g/cm³ | - |
| Solid Content | 93.0 | wt % | - |
| Specific Volume Resistance | min. 1 x 10¹⁰ | Ω.cm | Kö-test method 100262 |
| Value | Units | Test Method / Conditions | |
| Skin Formation Time | 45.0 | min | Kö-test method 100109, Climate according to DIN 50014 |
| Curing to Depth | 3.0 | mm/d | within first 24 h; Climate according to DIN 50014 |
| Change in Volume | -7.0 | % | DIN EN ISO 10563 |
| Hardness (after 28d, thickness of specimen = 6 mm) | 55.0 | - | DIN ISO 7619-1, Shore A |
| Tensile Strength | 4.0 | MPa | DIN EN ISO 527 |
| Elongation at Break | 400.0 | % | DIN EN ISO 527 |
| G10-Modulus | 1.3 | MPa | DIN EN 1465 |
| Lap Shear Strength (substrates: aluminum/aluminum) | 3.0 | MPa | DIN EN 1465 |
| Tear Strength | 7.0 | N/mm | ISO 34-1 |
| Value | Units | Test Method / Conditions | |
| Processing Temperature | 15 - 35 | °C | - |
| Required Squeezing Pressure | 2 - 5 | bar | - |
| Recommended Minimum Layer Thickness | 2.0 | mm | - |
| Value | Units | Test Method / Conditions | |
| Service Temperature | - 60 - 90 | °C | - |
| Short-Term Temperature Resistance (60 min) | 120.0 | °C | - |
Packaging & Availability
- Country Availability
- Regional Availability
Storage & Handling
- Storage Condition
Körapur 125 should be used within the shelf life specified on the packaging. The storage stability only applies to material stored in original unopened containers, at storage temperature 5°C to 25°C.