Enhanced TDS
Identification & Functionality
- Chemical Family
- Technologies
Features & Benefits
- Ready-to-Use Product Features
- Features and Benefits
- Green Anaerobic Retaining Compound and Sealant
- High Strength
- Fluorescent UV Indicator
- Excellent Gap and Void Filling Capability
- High Resistance to Heat, Corrosion, Vibrations, Water, Gasses, Oils, Hydrocarbons, and Many Chemicals
Applications & Uses
- Applications
- Application Area
- Cure Method
- General Instructions
Surfaces to be bonded should be clean and dry and free of grease. Product should be applied in enough quantity to fill all engaged threads or gap. The product performs best in thin bond gaps. Very large gaps may create gaps that will affect the cure speed and overall strength. Good contact is essential. It is recommended to confirm compatibility of the product with all substrates prior to use. This product is not recommended for use with strong oxidizing materials. Where aqueous washing systems are used to clean the surfaces before bonding, these aqueous washes can affect the cure and performance of the adhesive. This product is not normally recommended for use on plastics, users must check compatibility of the product with such substrates.
Properties
- Color
- Physical Form
- Physical Properties
- Chemical Resistance
- Cured Properties
- Uncured Properties
Value | Units | Test Method / Conditions | |
Heat Aging Testing (at 120°C, 1000 h) | 100.0 | % | - |
Heat Aging Testing (at 150°C, 1000 h) | 100.0 | % | - |
Value | Units | Test Method / Conditions | |
Room Temperature Strength (50% Water/50% Glycol, at 87°C, 1000h) | 80.0 | % | - |
Room Temperature Strength (Unleaded gasoline, at 22°C, 1000 h) | 85.0 | % | - |
Room Temperature Strength (Motor oil, at 125°C, 1000 h) | 100.0 | % | - |
Room Temperature Strength (Brake fluid, at 125°C, 1000h) | 80.0 | % | - |
Room Temperature Strength (Acetone, at 125°C, 1000 h) | 90.0 | % | - |
Value | Units | Test Method / Conditions | |
Cure Speed (at 5°C, 25% of room temperature strength) | 3.0 | h | - |
Cure Speed (at 5°C, 50% of room temperature strength) | 6.0 | h | - |
Cure Speed (at 5°C, 100% of room temperature strength) | 24 - 72 | h | - |
Cure Speed (at 40°C, 25% of room temperature strength) | 7.0 | min | - |
Cure Speed (at 40°C, 50% of room temperature strength) | 8.0 | min | - |
Cure Speed (at 40°C, 100% of room temperature strength) | 2 - 72 | h | - |
Cure Speed on Steel (25% of room temperature strength) | 22.0 | min | - |
Cure Speed on Steel (50% of room temperature strength) | 34.0 | min | - |
Cure Speed on Steel (100% of room temperature strength) | 18 - 72 | h | - |
Cure Speed on Aluminum (25% of room temperature strength) | 2.0 | h | - |
Cure Speed on Aluminum (50% of room temperature strength) | 15.0 | h | - |
Cure Speed on Zinc Dichromate (25% of room temperature strength) | 22.0 | min | - |
Cure Speed on Zinc Dichromate (50% of room temperature strength) | 34.0 | min | - |
Cure Speed on Zinc Dichromate (100% of room temperature strength) | 18 - 72 | h | - |
Cure Speed for 0.05mm Gap Size (25% of room temperature strength) | 28.0 | min | - |
Cure Speed for 0.05mm Gap Size (50% of room temperature strength) | 35.0 | min | - |
Cure Speed for 0.05mm Gap Size (100% of room temperature strength) | 10 - 72 | h | - |
Cure Speed for 0.25mm Gap Size (25% of room temperature strength) | 40.0 | h | - |
Cure Speed for 0.25mm Gap Size (50% of room temperature strength) | 70.0 | h | - |
Value | Units | Test Method / Conditions | |
Flash Point | min. 93 | °C | - |
Viscosity (Spindle 3, 20 rpm) | 1400.0 | cP | Brookfield RVT |
Specific Gravity | 1.11 | - | - |
Set Time (Steel) | 12 - 72 | h | - |
Full Cure Conditions | 12 - 72 | h | - |
Specific Heat | 0.3 | kJ/kgK | - |
Coefficient of Thermal Expansion | 80.0 | ppm/K | ASTM D696 |
Thermal Conductivity | 0.1 | W/m.K | ASTM C177 |
Service Temperature | - 55 - 150 | °C | - |
Pin/Collar Shear Strength | 22 - 40 | N-m | ISO 10123 |
Technical Details & Test Data
- Curing Performance
The rate of cure will depend on environmental conditions and the substrates used. The gap of the bond line will affect set speed. Smaller gaps tend to increase set speed. Activators may be applied to further improve set speed, but may also impair overall adhesive performance.
- Hot Strength (%RT strength, tested at temperature)
Storage & Handling
- Shelf Life
- 12 Months
- Storage Conditions
- Storage Temperature: 8 to 28°C.
- Products should be stored unopened in a cool, dry place out of direct sunlight. Products may be refrigerated for improved shelf life, but should be brought back to room temperature before use.