H.B. Fuller EA6053H is a fast-curing adhesive that utilizes UV light to cure. The product possesses a soft and flexible nature, while also exhibiting excellent adhesion properties. This adhesive can be used as a replacement for silicone rings in buffering applications. It is capable of providing good adhesion to a variety of substrates, including glass, plastics, and metals.

Product Type: 1K (1 component) Adhesive, Radiation Curable Adhesive

Application Area: Electronic Components

Compatible Substrates & Surfaces: Glass, Metal, Plastics

Chemical Family: Acrylics & Acrylates

Features: Fast Curing, Flexible, Good Adhesion, Soft, UV Curable

Technical Data Sheet

Enhanced TDS

Identification & Functionality

Features & Benefits

Ready-to-Use Product Features
Features and Benefits
  • One component, requires no mixing.
  • Fast curing.
  • Good adhesion to glass, many plastics and many metals.
  • Good flexible.

Applications & Uses

Markets
Applications
Application Area
Compatible Substrates & Surfaces
Instruction for Use

1. Coating surface area should be clean and free of any fluxes, residues, dust or any other contaminants.

2. A UV lamp with a wavelength of 365nm is required. The UV light should be focused towards the coated surface.

3. Curing speed is determined by the intensity of UV radiation, the distance from the UV light source and the coating surface. The depth of coating material can also require additional cure time.

4. Immediately close the lid after use. A black hose must be used to dispense the adhesive.

5. This material should be stored away from sunlight, UV light and artificial light sources.

Properties

Color (Properties)
Physical Form
Appearance
Semi translucent paste
Physical Properties of Cured Material
ValueUnitsTest Method / Conditions
Hardness (at 25°C, 100 mW/cm², at 365 nm, 24s)37.0-Shore A
Hardness (at -30°C, 100 mW/cm², at 365 nm, 24s)50.0-Shore A
Lap Shear Strength (Polycarbonate - Fr₄, 100 mW/cm², at 365 nm, 24s)6.0MPa-
Elongation at Break (100 mW/cm², at 365 nm, 24s)255.0%-
Lap Shear Strength (Polycarbonate - Polycarbonate, 100 mW/cm², at 365 nm, 24s)3.0MPa-
Uncured Properties
ValueUnitsTest Method / Conditions
Viscosity (25°C, CP52, 100 rpm)30550.0cP-
Thixotropic Index3.7--
Density1.05g/cm³-
Typical Cured Properties
ValueUnitsTest Method / Conditions
Tack Free Time (100 mW/cm², at 365 nm)max. 6s-
Depth of Cure (100 mW/cm², at 365 nm, 24sec)8.0mm-
Cure Energy2400.0mJ/cm²-

Technical Details & Test Data

Curing Profile

Recommended cure:

  • 100mW/cm2 @ 405nm for 30s

Safety & Health

Health and Safety Precautions

Keep away from children's store.
This product is recommended to be used within a well-ventilated place.
If you accidentally touches the skin, immediately wash with soap and water.
If you accidentally touches the eyes, please rinse with plenty of water, and then seek medical attention.

Packaging & Availability

Regional Availability
  • Africa
  • Asia Pacific (Excluding Russia)
  • Europe (Excluding Russia)
  • India
  • Latin America
  • Middle East
  • North America

Storage & Handling

Shelf Life
12 Months
Storage Conditions

Product should be stored at temperature between 8℃ to 28℃ in the unopened container in a dry location.