Enhanced TDS
Identification & Functionality
- Chemical Family
- RTU Product Type
- Technologies
- Product Families
Features & Benefits
- Ready-to-Use Product Features
Applications & Uses
- Markets
- Applications
- Application Area
- Compatible Substrates & Surfaces
- Cure Method
- Segment
- General Instructions
Surfaces to be bonded should be clean and dry. Dispense a drop or drops to one surface only. Apply only enough to leave a thin film layer after compression. Press parts together and hold firmly for a few seconds. Good contact is essential. An adequate bond develops in less that one minute and maximum strength is attained in 24 hours. Wipe off excess adhesive from the top of the container and recap. products if left uncapped may deteriorate by contamination from moisture in the air. Because products cure by polymerization, whitening may appear on the surface of the container or the bonded materials. This will not affect adhesive performance.
Properties
- Physical Form
- Appearance
- Clear
- Typical Properties
Value Units Test Method / Conditions Shear Strength* 4035 psi - Temperature Range -67 to 203 °F - Fixture Time 10 sec - Storage Temperature 15.5 - 25 °C - - Technical Data
Value Units Test Method / Conditions Density 1.06 g/cm³ - Specific Gravity 1.06 - - - Cured Properties
Value Units Test Method / Conditions Cure Time (Full) 24 h - Pressure (Performance of Cured Adhesive, ABS) 2110 - 2540 psi ASTM 4501 Pressure (Performance of Cured Adhesive, AL) 2070 - 2330 psi - Pressure (Performance of Cured Adhesive, PC) 3375 - 4035 psi ASTM 4501 Pressure (Performance of Cured Adhesive, PVC) 2570 - 3545 psi ASTM 4501 Pressure (Performance of Cured Adhesive, Rubber) 690 - 2200 psi - Pressure (Performance of Cured Adhesive, Steel) 2000 - 2460 psi - Service Temperature - 55 to 95 °C Cure Appearance Clear - - - Uncured Properties
Value Units Test Method / Conditions Set Time (Beech wood) min. 45 s - Flash Point 85.0 °C - Set Time (Ethylene Propylene Diene Monomer) 2 s - Set Time (acrylonitrile butadiene styrene) 10 s - Set Time (steel) 7 s - - Application Properties
Value Units Test Method / Conditions Relative Humidity 40 - 70 % - Handling Temperature 20 - 24 °C - - Rheological Properties
Value Units Test Method / Conditions Viscosity (at 20 - 25°C) 90 - 125 cPs Brookfield SC4-27 - Note
- * Performance of cured adhesive on Polycarbonate, tested to ASTM 4501
Regulatory & Compliance
- Certifications & Compliance
Technical Details & Test Data
- Solvent Resistance
Solvent Resistance Resistance Level Examples Alcohol Excellent Ethanol, Methanol, Isopropanol
Aliphatic hydrocarbons (alkanes) Very good Petrol, Heptanes, Hexane
Aromatic hydrocarbons Very good Benzyl, Toluol, Xylol
Ester (aliphatic) Poor Ethylacetate Halogenated hydrocarbons Poor Methylenchloride, Chloroform, Chlorobenzol
Ketone Poor Acetone, Benzophenone
Weak aqueous acid Excellent diluted nitrite, muriatic acid, sulphuric acid, phosphoric acid
Concentrated Acid Poor nitric acid, muriatic acid, sulphuric acid, phosphoric acid
Weak aqueous base Excellent diluted sodium hydroxide solution, caustic potash solution
Concentrated Base Poor sodium hydroxide solution, caustic potash solution
Water Very good - Technical Data
Figure 1: Strength of Cured Adhesive
Figure 2: Hot Strength (%RT strength, tested at temperature)
Figure 3: Time Until Full Cure
Figure 4: Heat Ageing on Steel (aged at temp. indicated and tested @ 20°C)
Figure 5: Durability after Alternating Climate Storage
- Curing Performance
Ambient surface moisture initiates the curing process. Handling strength is reached in a short time, and will vary based on environmental conditions, bond line gap, and other factors. Product will continue to cure for at least 24 hours before full strength and solvent resistance is developed.
- Technical Information
Technical User Information:
- Cyanoacrylates are fast setting, one component, and solvent-free adhesives.
- Polymerization is initiated by present humidity. Best results are given between 40 to 70% relative humidity and 20 to 24 °C ambient temperature.
Processing Information:
- Surfaces should be clean and free from grease. Dispense adhesive to one surface only. Apply only enough to leave a thin film layer after compression.
- Press parts together and hold firmly until the adhesive has fixtured. Maximum strength is attained typically in 24 hours. The product should be allowed to develop full strength before subjecting it to any service loads.
- Time Until Full Cure (% of RT strength)
- Performance Range by Substrate (N/mm²)
- Heat Aging (aged at temperature indicated and tested at 22°C)
- Hot Strength (%RT strength, tested at temperature)
- Performance of Cured Adhesive
Substrate N/mm² PSI Steel 13.8 to 17.0 2000 to 2460 Rubber* 4.8 to 15.2 690 to 2200 AL 14.3 to 16.1 2070 to 2330 PC** 23.3 to 27.8 3375 to 4035 PVC** 17.7 to 24.4 2570 to 3545 ABS** 14.5 to 17.5 2110 to 2540 *Rubber figures given are typical. Your results may vary by specific rubber type.
**Tested to ASTM 4501
***n/r = not recommended- Solvent Resistance
Solvent Example Resistance Alcohol Ethanol, Methanol
+ + + Ester (aromatic) Ethylacetate + + + Ketone (aromatic) Acetone, Benzophenone
– – – Aliphatic hydrocarbon (alkanes) Petrol, Heptanes, Hexane
+ + – Aromatic hydrocarbons Benzyl, Toluol, Xylol
+ + – Halogenated hydrocarbons Methylenchloride, Chloroform, Chlorobenzol
– – – Weak aqueous Nitrite, muriatic acid, sulphuric acid, phosphoric acid
+ + + (– – – if concentrated) Weak aqueous base sodium hydroxide solution, caustic potash
+ + + (– – – if concentrated)
Packaging & Availability
Storage & Handling
- Shelf Life
- 12 Months
- Storage Condition
- Cyberbond 2611 should be used within the shelf life specified on the packaging.
- The storage stability applies to material stored under appropriate conditions only (original unopened containers, recommended storage temperature).
- This product should be stored unopened in a cool, dry place out of direct sunlight.
- Storage Conditions
Containers should be stored in a cool, dry, dark area. Storage temperature 15.5°C - 25°C (60°F - 77°F), without exposure to direct light or heat. Do not refrigerate.