Enhanced TDS
Identification & Functionality
- RTU Product Type
- Technologies
- Product Families
Features & Benefits
- Ready-to-Use Product Features
- Product Highlights
- Designed for easy handling process.
- Application temperature (25°C) before cure – allows application and bonding to a wider range of heat sensitive materials.
- Will have more than 60% of cure strength with 4 hours of dispensing depending on RH and temperature.
- Open time of 4 minutes allowing for extended assembly time.
- High green strength allows immediate handling processing and testing.
- Adhesive forms a tough polymer bond resulting in excellent impact resistance and strong bonds.
- Dispenses like a one-part adhesive, but reacts over time to form a strong cross-linked network like a tough urethane polymer.
- Good adhesion to a wide range of substrates: metals, ceramics, plastics, coated wires – even woven fabrics. No need for primers.
Applications & Uses
- Markets
- Applications
- Application Area
- Compatible Substrates & Surfaces
- Cure Method
- Segment
- Product Application
- EH9363 can be dispensed using automatic dispensing or dipping systems at temperatures of 20-35°C.
- Green adhesion will be achieved as soon as the adhesive bond has cooled.
Properties
- Physical Form
- Cured Mechanical Properties
Value Units Test Method / Conditions Young’s Modulus 15 Mpa ASTM D638 Elongation at Break 450 % ASTM D638 Tensile Lap Shear Adhesion (PC-PC after 24 hours of cure) 4.5 Mpa ASTM D1002 - Uncured Properties
Value Units Test Method / Conditions Specific Gravity 1.05 - - Solid Content 100.0 % - Viscosity (at 25°C) 50 - 70 cPs - - Application Properties
Value Units Test Method / Conditions Application Temperature 20 - 35 °C - Open Time (time within which substrates must be bonded without reheating) 3 - 5 m - - Clean Up
- Any uncured residual adhesive can be scraped off using a blade. After scraping, wipe clean with a common polyurethane solvent (toluene, MEK). Clean up the adhesive residue before it cures.
- If the dispense equipment is to be shut down for extended periods of time.Partially used containers of EH9363 should be purged with a dry inert gas and resealed between uses.
- Cure Properties
- The chemical reaction that results in cross-linking begins in the presence of low levels of atmospheric moisture. The rate of cross-linking will vary depending on temperature, humidity, and thickness. Please consult with your HB Fuller technical representative for additional recommendations.
Packaging & Availability
- Regional Availability
Storage & Handling
- Storage Information
- EH9363 should be stored in its original sealed foil bag in a dry location that maintains temperatures between 15˚C to 35°C. Shelf life is 6 months in original unopened (sealed) foil bag when stored at this temperature range.