Enhanced TDS
Identification & Functionality
- Chemical Family
- Product Type
- Technologies
- Product Families
Features & Benefits
Applications & Uses
- Markets
- Applications
- Application Area
- Cure Method
- Curing Profile
Recommended cure: 21 - 25°C, 45 - 55%RH for 7 days
- Application Instructions
- Part A should be blended thoroughly before mix with Part B in order to make filling material distribute evenly.
- Mix evenly according to the ratio.
- Pot the mixed material.
- Recommended using automatic dispensing equipment to applying the potting compound.
Properties
- Color (Properties)
- Physical Form
- Appearance
- White viscous liquid
- Thermal Properties
Value Units Test Method / Conditions Thermal Service Range - 50 - 200 °C - Thermal Conductivity 0.3 W/m.K DIN EN 821 - Cured Mechanical Properties
Value Units Test Method / Conditions Hardness 45.0 - GB/T 531, Shore A Tensile Strength 1.0 MPa GB/T 528 Elongation at Break 100.0 % GB/T 528 - Electrical Properties
Value Units Test Method / Conditions Volume Resistivity 1.0 x 10¹⁵ Ω.cm GB/T 1692 Breakdown Strength 20.0 kV/mm GB/T 1695 - Technical Data
Value Units Test Method / Conditions Mixed Density 1.26 g/cm³ GB/T 13354 Volumetric Mix Ratio 4:1 - - Weight Mix Ratio 5.5:1 - - Viscosity 1000 - 3000 cP - Working Time min. 8 min - - Cured Properties
Value Units Test Method / Conditions Flash Point min. 93 °C GB/T 5208 Working Time (Viscosity higher than 30000 mPa·s) 8.0 min - Gel Time 60.0 min - - Damp Heat Aging Test Properties
Value Units Test Method / Conditions Volume Resistivity (at 85°C, 85% RH, 1000h) 1.0 x 10¹⁵ Ω.cm GB/T 1692 - Rheological Properties
Value Units Test Method / Conditions Viscosity (Resin) 4000.0 mPa.s GB/T 2794 Viscosity Activator 50.0 mPa·s GB/T 2794 Viscosity (Mixed) 2000.0 mPa.s GB/T 2794
Packaging & Availability
- Country Availability
- Regional Availability
Storage & Handling
- Shelf Life
- 6 Months
- Storage Condition
Product shall be ideally stored in a cool, dry area in unopened containers at room temperature. Keep away from children.