H.B. Fuller EA6201

H.B. Fuller EA6201 is a fast, UV/thermal dual-curable acrylate adhesive. This product is suitable for bonding a wide variety of substrates, including glass, many plastics, and most metals. H.B. Fuller EA6201 has shown excellent adhesion and is flexible after curing.

Product Type: 1K (1 component) Adhesive, Radiation Curable Adhesive

Compatible Substrates & Surfaces: Glass, Metal, Plastics

Chemical Family: Acrylics & Acrylates

Features: Fast Curing, Good Adhesion, Highly Flexible, UV Curable

Technical Data Sheet
Message our experts with questions
Robert Blackstone avatar

Robert Blackstone

Global Leader - Inside Sales

Please reach out to me with any questions, I am happy to assist you in finding the right product or learning more about our storefront

Enhanced TDS

Identification & Functionality

Chemical Family

Features & Benefits

Features and Benefits
  • Can cure at room temp with P13115 primer
  • Good adhesion to glass, many plastics and metals
  • Flexible after cure

Applications & Uses

Compatible Substrates & Surfaces
Cure Method
Instruction for Use

1. Prior to bonding, surfaces must be free of any dust, oils, or other contaminants.
2. A UV lamp with a wavelength of 365nm is required; the UV light should be focused on the coated surface.
3. Curing speed is determined by the intensity of UV radiation, the distance from the UV light source and the coating surface. The depth of coating material can also affect cure time.
4. Immediately close the lid after use. A black hose must be used to dispense the adhesive.
5. This material should be stored away from sunlight, UV light and artificial light sources.


Uncured Properties
ValueUnitsTest Method / Conditions
Thixotropic Index4.1--
Surface Tack-Free Time (at 100 mW/cm²)max. 10s-
Depth of Cure (at 24sec)6.0mm-
Typical Cured Properties
ValueUnitsTest Method / Conditions
Hardness (100 mW/cm², at 365 nm, 24s)62.0-Shore D
Tensile Strength (at Break, 100 mW/cm², at 365 nm, 24s)19.6MPa-
Elongation at Break (100 mW/cm², at 365 nm, 24s)139.0%-
Young’s Modulus (100 mW/cm², at 365 nm, 24s)333.7MPa-
Glass Transition Temperature (100 mW/cm², at 365 nm, 24s)52.3°C-
Lap Shear Strength (Polycarbonate, 100 mW/cm², at 365 nm, 24s)7.2MPa-
Lap Shear Strength (Glass - Aluminum, 100 mW/cm², at 365 nm, 24s)9.5MPa-
Surface Resistivity (100 mW/cm², at 365 nm, 24s)8.0 x 10¹⁴ohm-
Volume Resistivity (100 mW/cm², at 365 nm, 24s)8.0 x 10¹⁴ohm-
Dielectric Breakdown Strength (100 mW/cm², at 365 nm, 24s)22.0kV/mm-
Dielectric Constant (at 1MHZ, 100 mW/cm², at 365 nm, 24s)4.2--
Dissipation Factor (at 1MHz, 100 mW/cm², at 365 nm, 24s)0.03--
Fixture Time (One side with P13115, 25°C for 24 hours)4.0min-
Lap Shear Strength (Aluminum, One side with P13115, 25°C for 24 hours)15.7MPa-
Cure Energy2400.0mJ/cm²-

Technical Details & Test Data

Cure Conditions
  • 100mW/cm² @ 365nm for 24s +
  • One side with P13115 primer, 25C for 24hrs
    • 80°C for 90min
    • 120°C for 60min

Packaging & Availability

Regional Availability
  • Africa
  • Asia Pacific (Excluding Russia)
  • Europe (Excluding Russia)
  • India
  • Latin America
  • Middle East
  • North America

Storage & Handling

Shelf Life
6 Months
Storage Conditions

EA6201 should be sealed and stored in original container between 8ºC and 28ºC in a dry, dark place.
Shelf life at these conditions is 6 months from date of manufacture.