Enhanced TDS
Identification & Functionality
- Chemical Family
- Technologies
- Product Families
Features & Benefits
- Ready-to-Use Product Features
Applications & Uses
- Markets
- Applications
- Application Area
- General Instructions
Surfaces to be bonded should be clean and dry and free of grease. Product should be applied in enough quantity to fill all engaged threads. The product performs best in thin bond gaps. Very large gaps may create gaps that will affect the cure speed and overall strength. Good contact is essential. An adequate bond develops in 15 to 45 minutes and maximum strength is attained in 24 hours. This product is not recommended for use in pure oxygen environments and/or oxygen-rich systems and should not be slected as a sealant for chlorine or other strong oxidizing materials. This product is not designed for plastics, particularly thermoplastics where stress cracking of the plastic could result. It is recommended to confirm compatibility of the product with all substrates prior to use.
Properties
- Color
- Physical Form
- Cured Mechanical Properties
- Technical Data
- Cured Properties
- Uncured Properties
- Rheological Properties
- Specifications
Mil-S-46163A, Type I Grade L; ASTM D-5363 AN 0211
| Value | Units | Test Method / Conditions | |
| Locking Strength | high | — | — |
| Service Temperature | - 55 - 150 | °C | — |
| Breakaway Torque | min. 150 | — | — |
| Prevailing Torque | min. 200 | — | — |
| Value | Units | Test Method / Conditions | |
| Specific Gravity | 1.1 | — | — |
| Value | Units | Test Method / Conditions | |
| Full Cure Conditions | 24.0 | h | — |
| Cure Appearance | Red solid | — | — |
| Value | Units | Test Method / Conditions | |
| Flash Point | min. 93 | °C | — |
| Gap Fill | 0.016 | inch | — |
| Value | Units | Test Method / Conditions | |
| Viscosity (at 0.50 rpm) | 5500 - 8000 | cP | Brookfield |
Technical Details & Test Data
- Curing Performance
The rate of cure will depend on environmental conditions and the substrates used. The gap of the bond line will affect set speed. Smaller gaps tend to increase set speed. Activators may be applied to further improve set speed, but may also impair overall adhesive performance.
- Set Time on Various Substrates
- Heat Aging (aged at temperature indicated and tested at 22°C)
- Hot Strength (%RT strength, tested at temperature)
- Solvent Resistance
Solvent Example Resistance Alcohol Ethanol, Methanol
+ + + Ester (aromatic) Ethylacetate – – – Ketone (aromatic) Acetone, Benzophenone
– – – Aliphatic hydrocarbon (alkanes) Petrol, Heptanes, Hexane
+ + – Aromatic hydrocarbons Benzyl, Toluol, Xylol
+ + – Halogenated hydrocarbons Methylenchloride, Chloroform, Chlorobenzol
– – – Weak aqueous Nitrite, muriatic acid, sulphuric acid, phosphoric acid
+ + + (– – – if concentrated) Weak aqueous base sodium hydroxide solution, caustic potash
+ + + (– – – if concentrated)
Packaging & Availability
- Regional Availability
Storage & Handling
- Shelf Life
- 12 Months
- Storage Conditions
- Storage Temperature: 20°C.
- Products should be stored unopened in a cool, dry place out of direct sunlight. Products may be refrigerated for improved shelf life, but should be brought back to room temperature before use.