H.B. Fuller EV Bond 383
1 of 264 products in this brandRTU Product Type: 2K (2 component) Adhesive, Epoxy Adhesive, Structural Adhesive
Application Area: Batteries, Battery Packs, Electric Vehicle (EV)
Compatible Substrates & Surfaces: Aluminum, Composites, Metal, Steel
Chemical Family: Epoxy & Epoxy Derivatives
Features: Ambient Curing, Bright Fluorescence, Good Bonding Strength, Good Elongation, Heat Resistance, High Impact Resistance, Long Open Time, Peel Resistance, Thixotropic, Toughened
Enhanced TDS
Identification
- Chemical Family
- GBU
- RTU Product Type
- Categories
Applications
- Application Area
- Compatible Substrates & Surfaces
Applications & Uses
- Mixing and Curing
-
Mixing and Curing Schedule
Ratio Part A Part B By weight 100 86 By volume 1 1 The recommended cure schedule to achieve the typical properties is 5 days at 25°C/77°F. Properties will be slightly altered if exposed to elevated temperature post-cure.
Features
- Ready-to-Use Product Features
Identification & Functionality
- Base
-
Epoxy
Packaging & Availability
- Packaging Type
- Regional Availability
- Typical Packaging
-
- 200 mL Cartridge
- 5 gallon Pail
- 55 gallon Drum
Properties
- Density:
-
1090 kg/m³
- Glass Transition Temperature (Tg):
-
53 °C
- Shelf Life:
-
12 months
- Specific Gravity:
-
1.09
- Tensile Strength:
-
30.9948 MPa
- Viscosity:
-
27000 cps
- Physical Properties
-
Value Units Test Method / Conditions Coefficient of Thermal Expansion (at 30 - 40°C) 111.8 ppm/°C - Glass Transition Temperature 53 °C - Mixing and Curing Schedule (at 25°C, by volume, 5 days cure) 1:1 - - Mixing and Curing Schedule (at 25°C, by volume, part A, 5 days) 1 - - Mixing and Curing Schedule (at 25°C, by weight, 5 days cure) 100:86 - - Mixing and Curing Schedule (at 25°C, by weight, part B, 5 days) 80 - - Tensile Elongation (at 25°C, break) avg. 14.3 % - Tensile Strength (at 25°C) avg. 4492 psi - - Component B
-
Value Units Test Method / Conditions Density 8.42 lbs/gal - Specific Gravity (at 25°C) 1.01 - - Viscosity (at 25°C) 23000 cPs - - Uncured Properties
-
Value Units Test Method / Conditions Density (blend uncured) 8.85 lbs/gal - Gel Time (at 25°C, 200g, mixed uncured) 54 minutes - Specific Gravity (at 25°C, blend uncured) 1.09 - - Tack-Free Time (at 25°C, blend, 40mil layer uncured) 180 minutes - Viscosity (at 25°C, blend uncured) 27000 cPs - - Component A
-
Value Units Test Method / Conditions Density 9.1 lbs/gal - Specific Gravity (at 25°C) 1.177 - - Viscosity (at 25°C) 34000 cPs - - Typical Properties
-
Value Units Test Method / Conditions Storage Temperature 16 - 27 °C - - Typical Cured Properties
-
Value Units Test Method / Conditions Tensile Lap Shear (at 25°C, 5 day cure at 25°C, 5mil bondline thickness, sandblasted cold rolled steel) 3203 psi - Tensile Lap Shear (at 25°C, 5 day cure, 5mil bondline thickness, scoured aluminum) 2413 psi - Tensile Lap Shear (at 25°C, 5 day cure, 5mil bondline thickness, solvent wiped aluminum) 2173 psi -
Safety & Health
- Safety Information
-
Although the system contains low volatility materials, care should be taken in handling. Use adequate ventilation in the work area. These materials may cause dermatitis in susceptible individuals. Keep off skin and out of eyes. In case of accidental skin contact, wash thoroughly with soap and water. In case of eye contact, flush eyes thoroughly with water and consult a physician immediately.
Storage & Handling
- Storage and Shelf Life
-
These materials should be stored in a dry environment within a temperature range of 16 °C to 27 °C (60 °F to 80 °F). Extremes of temperature beyond this range may result in crystallization or polymerization of the materials. Introduction of a nitrogen blanket into the containers before closing will improve the storage life of the products.
- Shelf Life
-
12 months (in separate sealed containers, part A uncured), 12 months (in separate sealed containers, part B uncured)