H.B. Fuller MP5405NS
1 of 264 products in this brandH.B. Fuller MP5405NS is a two-part unfilled epoxy adhesive that is designed for high-speed bonding of metals, ceramics, and most plastics. It cures to a tough, semi-rigid material and has a thixotropic paste consistency to prevent running and sagging. This product has good resistance to water, salt spray, inorganic acids and bases, and most organic solvents. It was specially formulated to a 1:1 mix ratio for use in either MMD equipment or side-by-side dual cartridges for easy dispensing. A handling cure is normally achieved at room temperature within 20 - 30 minutes, with full cure in 24 hours. An elevated temperature cure schedule can be used to reach final properties quickly.
Chemical Family: Epoxy & Epoxy Derivatives
RTU Product Type: 2K (2 component) Adhesive, Epoxy Adhesive, Reactive Adhesive, Structural Adhesive
Application Area: Cartridge
Compatible Substrates & Surfaces: Ceramic, Elastomers & Rubbers, Glass, Metal, Plastics
Features: Excellent Salt Spray Resistance, Free Flowing, Good Adhesion, Good Sagging Resistance, Good Toughness, Room Temperature Curing, Solvent Resistance, Thixotropic
-
Type Document Name
-
Technical Data SheetH.B. Fuller MP5405NS Technical Data Sheet
Enhanced TDS
Identification
- Chemical Family
- GBU
- RTU Product Type
- Categories
-
Applications
- Application Area
- Compatible Substrates & Surfaces
Applications & Uses
- General Instructions
-
- Surfaces to be bonded must be clean, dry and free of other contaminants.
- Bring both components to room temperature prior to mixing.
- Measure out specified amounts of parts A and B and stir (without introducing bubbles) until homogenous or use a static mixing nozzle.
- Apply the uniform mixture to both surfaces.
- Allow to cure while being held in place with light clamping.
Features
- Ready-to-Use Product Features
Packaging & Availability
- Regional Availability
Physical Properties
- Color (Properties)
- Physical Form
- Appearance
-
Translucent/white viscous paste
Properties
- Dielectric Strength:
-
16.1 kV/mm
- Strain at Break:
-
3~5 %
- Tensile Strength:
-
48.3 MPa
- Cured Properties
-
Value Units Test Method / Conditions Dielectric Constant (at 100Hz) 4.5 - ASTM D150 Dielectric Strength 16.1 kV/mm ASTM D149 Elongation at Break 3 - 5 % ASTM D638 Hardness 80 Shore D ASTM D2240 Operating Temperature - 40 to 130 °C - Overlap Shear Strength (at 25°C, 50% RH, aluminum, acid etched) 19.3 MPa ASTM D1002 Tensile Strength 48.3 MPa ASTM D638 Volume Resistivity 800000000000000 Ω-cm ASTM D257 - Uncured Properties
-
Value Units Test Method / Conditions Handling Time Full Cure (at 23°C) 20 - 30 minutes - Handling Time Full Cure (at 66°C) 24 hours - Mix Ratio (by volume) 1:1 - - Mix Ratio (by weight) 1:1 - - Pot Life (at 25°C, 20g) 3 - 5 minutes - Specific Gravity (mix) 1.16 - - Specific Gravity (part A) 1.17 - - Specific Gravity (part B) 1.15 - - - Typical Properties
-
Value Units Test Method / Conditions Storage Temperature 12 - 25 °C - - Rheological Properties
-
Value Units Test Method / Conditions Viscosity (at 25°C) 1500000 cPs - - Component A
-
Value Units Test Method / Conditions Viscosity (at 25°C) 1500000 cPs - - Component B
-
Value Units Test Method / Conditions Viscosity (at 25°C) 1500000 cPs - - Appearance
-
Translucent/white viscous paste
Storage & Handling
- Storage Conditions
-
- Product should be stored in a cool and dry place out of direct sunlight.
- The shelf life is from date of manufacture.
- Shelf life is based on the products being stored properly at temperatures between 12°C and 25°C.
- Exposure to temperatures above 25°C will reduce the shelf life.
- This product should not be frozen.
- Shelf Life
-
12 months