ProSpec® Premium Patch 100

1 of 15 products in this brand
ProSpec® Premium Patch 100 is a fast-setting, fiber-reinforced, high-strength cement-based repair mortar that provides quick early strength gain, minimizing downtime for repair applications.

Product Type: Repair Mortar

Application Area: Bridge Deck, Freezer Rooms, Highway Repair, Loading Docks, Overlays, Parking Structures, Runway, Warehouses, Wastewater Treatment Facilities

Features: Alkali Resistant, Fast Setting, Fiberglass Reinforced, Good Impact Strength, High Durability, High Early Strength, High Performance, High Strength, High Tensile Strength, Improved Flexural Strength, Magnesium Phosphate-Free, Minimizes Downtime, Non Corrosive, Wide Temperature Operating Range

Enhanced TDS

Identification & Functionality

Features & Benefits

Labeling Claims
Ready-to-Use Product Features
Product Features and Benefits
  • Interior/exterior
  • High early strength – over 2000 psi (14 MPa) in one hour allows repairs to be opened to traffic within 60 minutes
  • Wide temperature range – from 20oF to 100oF (-6oC to 38oC)
  • Apply 1/2” to 2”
  • Can be extended up to 60% by weight for repairs greater than 2” (51 mm) deep
  • High performance cement technology and alkali resistant fibers help improve impact, flexural and tensile strengths
  • Cement based, non-corrosive – not a chemical concrete
  • Contains corrosion inhibitor
  • Contains no chlorides or magnesium phosphates
  • Compatible with portland cement formulated concrete
  • Suitable for DOT horizontal concrete repairs
  • Meets ASTM C 928, Standard Specification for Packaged, Dry, Very Rapid, Hardening Cementitious Materials for Concrete Repair

Applications & Uses

Markets
Applications
Application Area
Compatible Substrates & Surfaces
Cure Method
Product Applications

Uses :
Concrete repair mortar designed to repair heavy duty surfaces such as:

  • Highway repairs and overlays
  • Bridge decks and parking structures
  • Airport runways
  • Freezer rooms
  • Heavy industrial and warehouse repairs
  • Loading docks and wastewater treatment facilities

Installation:

Preparation: All materials should be stored at 40°F (4°C) to 80°F (27°C) 24 hours prior to installation. Surfaces must be solid, clean, free of all bond breakers such as oil, grease, dirt etc. Weak concrete surfaces must be cleaned down to solid sound concrete by mechanical means.

  • The base concrete should be roughened to enhance mechanical bond and repair areas should be in a saturated surface dry (SSD) condition with all standing water removed. Using a stiff broom or brush apply a bond scrub coat of thinly mixed Premium Patch 100 to the adjacent surfaces.
  • Do not let this bond coat dry, before covering it with Premium Patch 100. A minimum patch repair depth of 1/2” (13 mm) is required. This is best accomplished by saw cutting the patch area perimeter to the minimum 1/2” (13 mm) depth.
  • Note: It is the responsibility of the installer/applicator to ensure the suitability of the product for its intended use.

Application: Ideal application conditions are when air, material and substrate temperature are between 40°F (4°C) and 80°F (27°C). For applications outside this range of temperatures, contact ProSpec® Technical Services.

Hot and Cold Weather Applications: Ideal mixed product temperature at placement is 65o - 70oF (18o - 21oC), where the initial setting time is 20 - 30 minutes. Hot temperatures will shorten setting time, while cold temperatures will extend setting time.

Hot Weather °F to 100°F (27°C to 38°C): Keep Premium Patch 100 cool. Pre-soak and then remove standing water from the repair area, resulting in a saturated surface dry (SSD) surface. Mix Premium Patch 100 using ice water to extend working time. The repair must be protected from rapid dry out with wet burlap or a water-based curing compound.

Cold Weather 20°F to 40°F (-7°C to 4°C): Do not use antifreeze or accelerators and keep Premium Patch 100 warm. Heat the surrounding concrete until warm. Combine the warmed repair material with warm mixing water. After placing use a construction insulating blanket for at least 2 - 3 hours and keep material from freezing.

Job Mockups: The manufacturer requires that when its ProSpec® products are used in any application or as part of any system that includes other manufacturers’ products, the contractor and/or design professional shall test all the system components collectively for compatibility, performance and long-term intended use in accordance with pertinent and accepted industry standards prior to any construction. Written documentation of the tests performed shall be satisfactory to the design professional and contractor. Test results must include the means and methods of application, products used, project-specific conditions being addressed, and standardized tests performed for each proposed system or variation.

Mixing:

  • Mix as close to the area being repaired as possible. Premium Patch 100 requires only the addition of water. Use 2.5 qt (2.4 L) per 50 lb (22.7 kg). Place the potable water into the mixing container and then while mixing add the repair material.
  • The Premium Patch 100 can be mixed in a mortar mixer or by using a paddle attached to a heavy duty 1/2” drill (650 rpm). Mix for 2 - 3 minutes to a lump free consistency. Do not re- temper or overwater.
  • Place immediately after mixing, working Premium Patch 100 firmly into the sides and bottom eliminating air pockets and ensuring bond. This is best done working from one side of the cavity to the other and then screeding toward the adjoining concrete.
  • For repairs deeper than 2” (5 cm), Premium Patch 100 can be extended 60% by weight using clean 3/8” (10 mm) dry pea gravel. Mix the Premium Patch 100 as outlined and then during the last minute of mixing (after 2 minutes) add the pea gravel, blend for 1 additional minute and place.

Curing: Premium Patch 100 should be moist cured for 1 hour after final set (approximately 20 minutes) or the application of a water- based curing compound is acceptable. Prolonged wet curing minimizes the chances of cracking and improves physical properties.

Cleaning:
Use water to clean all tools immediately after use.
Limitations:

  • Do not use for applications less than 1/2” (13 mm) thick.
  • Do not retemper after mixing.
  • Do not overwater or add other cements or additives.
  • Protect from premature drying.

Coverage:

  • 50 lb (22.7 kg) yields approximately 0.4 ft3 (0.01 m3).
  • 50 lb (22.7 kg) extended with 30 lb (13.6 kg) of 3/8” (10 mm) pea gravel yields approximately 0.7 ft3 (0.02 m3).

Properties

Physical Form
Technical Data
ValueUnitsTest Method / Conditions
Set Time (Initial Set)37.0minASTM C 191 (vicat)
Set Time (Final Set)46.0min-
Flow128.0-ASTM C 1437
Compressive Strength (at 45°F , 3 hours)2980.0psiASTM C 109
Compressive Strength (at 45°F , 1 day)8250.0psiASTM C 109
Compressive Strength (at 45°F , 7 days)10390.0psiASTM C 109
Compressive Strength (at 45°F , 28 days)10810.0psiASTM C 109
Compressive Strength (at 73°F , 3 hours)4830.0psiASTM C 109
Compressive Strength (at 73°F , 1 day)6750.0psiASTM C 109
Compressive Strength (at 73°F , 7 days)8330.0psiASTM C 109
Compressive Strength (at 73°F , 28 days)9270.0psiASTM C 109
Compressive Strength (at 95°F , 3 hours)4720.0psiASTM C 109
Compressive Strength (at 95°F , 1 day)6890.0psiASTM C 109
Compressive Strength (at 95°F , 7 days)8860.0psiASTM C 109
Compressive Strength (at 95°F , 28 days)9930.0psiASTM C 109
Length Change (1” Prism, Air Cured (28 day))-0.067%ASTM C 157
Length Change (1” Prism, Water Cured (28 day))0.027%ASTM C 157
Length Change (3” Prism, Air Cured (28 day))-0.044%ASTM C 157
Length Change (3” Prism, Water Cured (28 day))0.02%ASTM C 157
Shear Bond Strength (1 day)1500.0psiASTM C 882
Shear Bond Strength (7 days)1830.0psiASTM C 882
Shear Bond Strength (28 days)2000.0psiASTM C 882
Salt Scaling (25 cycles)0.0-ASTM C 672
Freeze/Thaw Resistance (300 cycles, F/T Durability, RDM)92.0%ASTM C 666 (B)
Freeze/Thaw Resistance (300 cycles, % weight loss)0.4%ASTM C 666 (B)
Freeze/Thaw Durability (50 cycles, Loss)0.0%NY 502-3P
Absorption (28 day)9.0%ASTM C 140
Chloride Content0.004% wtASTM C 1218
Flexural Strength470.0psiASTM C 78
Chloride Penetrability (28 day)2750.0CoulombsASTM C1202
Splitting Tensile Strength (28 day)550.0psiASTM C 496
Modules of Elasticity (28 day)4.06 x 10⁶psiASTM C469
Coefficient of Thermal Expansion (28 day)5.9 x 10⁻⁶in/in/°FASTM C 531

Regulatory & Compliance

Quality Standards

Packaging & Availability

Packaging Type
Regional Availability
  • North America

Storage & Handling

Shelf Life
12 months
Storage and Shelf Life Condition

12 months from the date of manufacture when stored in the original, unopened container, away from moisture, under cool, dry conditions and out of direct sunlight.