H.B. Fuller 2077

H.B. Fuller 2077 is a single-component, medium-viscosity cyanoacrylate adhesive. It is suitable for general-purpose bonding, particularly providing excellent strength and speed on all rubber compounds. H.B. Fuller 2077 is certified to ISO 10993-5, 10993-10, and 10993-11 for biocompatibility, making it suitable for use in medical applications.

Product Type1K (1 component) Adhesive, Reactive Adhesive

Application AreaMedical Devices

Compatible Substrates & SurfacesElastomers & Rubbers

Chemical FamilyCyanoacrylates

FeaturesChemical Resistant, General Purpose, Good Solvent Resistance, Medium Viscosity

Technical Data Sheet

Enhanced TDS

Identification & Functionality

Chemical Family

Features & Benefits

Applications & Uses

Application Area
Compatible Substrates & Surfaces
General Instructions

Surfaces to be bonded should be clean and dry. Dispense a drop or drops to one surface only. Apply only enough to leave a thin film layer after compression. Press parts together and hold firmly for a few seconds. Good contact is essential. An adequate bond develops in less that one minute and maximum strength is attained in 24 hours. Wipe off excess adhesive from the top of the container and recap. products if left uncapped may deteriorate by contamination from moisture in the air. Because products cure by polymerization, whitening may appear on the surface of the container or the bonded materials. This will not affect adhesive performance.

Properties

Physical Form
Appearance
Clear
Technical Data
ValueUnitsTest Method / Conditions
Viscosity650 - 950cP
Specific Gravity1.06
Cured Properties
ValueUnitsTest Method / Conditions
Service Temperature- 55 - 95°C
Full Cure Time24.0h
Cure AppearanceClear
Uncured Properties
ValueUnitsTest Method / Conditions
Flash Point85.0°C
Set Time (Ethylene Propylene Diene Monomer)4.0s
Set Time (Steel)35.0s
Set Time (Acrylonitrile Butadiene Styrene)6.0s
Specifications and Approvals

Mil-A-46050C, Type II Class III, A-A-3097, Type II Class 3

Regulatory & Compliance

Certifications & Compliance

Technical Details & Test Data

Curing Performance

Ambient surface moisture initiates the curing process. Handling strength is reached in a short time, and will vary based on environmental conditions, bond line gap, and other factors. Product will continue to cure for at least 24 hours before full strength and solvent resistance is developed.

Performance of Cured Adhesive
Substrate N/mm² PSI
Steel 13.8 to 18.8 2000 to 2730
Rubber* 5.1 to 15.2 735 to 2200
AL 3.1 to 3.5 450 to 510
PC** 22.3 to 24.9 3240 to 3605
PVC** 18.3 to 26.7 2660 to 3875
ABS** 12 to 18.3 1740 to 2660

 

*Rubber figures given are typical. Your results may vary by specific rubber type.
**Tested to ASTM 4501
***n/r = not recommended

Solvent Resistance
Solvent Example Resistance
Alcohol

Ethanol, Methanol

+ + +
Ester (aromatic) Ethylacetate + + +
Ketone (aromatic)

Acetone, Benzophenone

– – –
Aliphatic hydrocarbon (alkanes)

Petrol, Heptanes, Hexane

+ + –
Aromatic hydrocarbons

Benzyl, Toluol, Xylol

+ + –
Halogenated hydrocarbons

Methylenchloride, Chloroform, Chlorobenzol

– – –
Weak aqueous

Nitrite, muriatic acid, sulphuric acid, phosphoric acid

+ + + (– – – if concentrated)
Weak aqueous base

sodium hydroxide solution, caustic potash

+ + + (– – – if concentrated)
Time Until Full Cure (% of RT strength)

H.B. Fuller 2077 - Time Until Full Cure (% of Rt Strength)

Performance Range by Substrate (N/mm²)

H.B. Fuller 2077 - Performance Range By Substrate (N/Mm²)

Heat Aging (aged at temp indicated and tested at 22°C)

H.B. Fuller 2077 - Heat Aging (Aged At Temp Indicated And Tested At 22°C)

Hot Strength (%RT strength, tested at temperature)

H.B. Fuller 2077 - Hot Strength (%Rt Strength, Tested At Temperature)

Storage & Handling

Shelf Life
12 Months
Storage Conditions

Containers should be stored in a cool, dry, dark area. Storage temperature 15.5°C - 25°C (60°F - 77°F), without exposure to direct light or heat. Do not refrigerate.