Enhanced TDS
Identification & Functionality
- Backing Material Type
- Product Type
- Technologies
Features & Benefits
- Ready-to-Use Product Features
- Product Highlights
AT-1 offers numerous advantages including a waterproof bond, ease of application, and the ability to withstand thermal movement.
- Transparent appearance works well with applications involving glass or other clear materials
- Pressure sensitive bonding
- Solid composition for easy cutting
- Moisture resistant
- Excellent weathering properties
- Maintains adhesion at sub-zero temperatures
- Hardening or brittle resistant with age
- Flexible – conforms to intricate shapes
Applications & Uses
- Applications
- Compatible Substrates & Surfaces
- Typical Applications
- Auto trim attachment
- Signs
- Graphics
- Skin to frame assembly
- Furniture
- Appliances
- Many other manufacturing and construction applications to replace mechanical fasteners and welds
- General Application Instructions
- Substrate Evaluation : Acrylic adhesive is suitable for bonding a variety of substrates, including many plastic composites, sealed wood, and metals. Low surface energy materials such as polyethylene, polypropylene, silicones and PTFE can be difficult to bond to. Thorough evaluation is recommended when bonding to any questionable surface. An adhesion promoter (primer) for use with pressure sensitive acrylic adhesives may be necessary to facilitate proper bonding, and is available from H.B. Fuller.
- Preparation of Substrate : The substrate to be bonded should be cleaned with an appropriate solvent, preferably isopropanol (IPA). The acrylic adhesive backed part should be applied within 15 minutes of cleaning. To ensure removal of all contaminants without leaving any residue, use a clean, lint-free wiping cloth or disposable wipe. Never use recycled rags. Other solvents such as hexane, heptane, or methanol may be suitable for cleaning various substrates after thorough evaluation. The substrate must be completely dry through evaporation of the solvent with radiant heat, hot air dryers, or with time before bonding acrylic adhesive backed parts.
- Adhesive Promoter Application-If necessary: Apply the AP-1 Adhesion Promoter to the substrate(s) either with a lint-free applicator or foam brush. Apply the Adhesion Promoter in a “wet” laydown thickness range of 1-8 mils. Allow the Adhesion Promoter to dry approximately 5 minutes. Don’t touch the Adhesion Promoter.
- Application of Adhesive Backed Part to the Substrate: Remove the protective release liner from the acrylic tape immediately prior to applying the part to be bonded, being careful not to contaminate the acrylic adhesive. Apply within 15 minutes after surface preparation. Apply the part to be bonded without entrapping air between the tape and the substrate with a recommended minimum application pressure of 15 pounds per inch of tape width to achieve adhesive to substrate contact and maximum bond.
Properties
- Color
- Physical Properties
- Technical Data
| Value | Units | Test Method / Conditions | |
| Thickness | 0.25 - 1.5 | mm | — |
| Width | 6 - 457 | mm | — |
| Value | Units | Test Method / Conditions | |
| Tensile Strength | 1.7 | MPa | ASTM D412 Die C |
| Elongation | 1000.0 | % | ASTM D412 Die C |
| Dynamic Shear | 415.0 | kPa | ASTM D3163 |
| Static Shear (at 74°F,1000g, 1 in², 100hrs) | Pass | — | WSB-M3G138-B |
| Static Shear (at 158°F,1000g, 1 in², 100hrs) | Pass | — | WSB-M3G138-B |
| Adhesion (90° Peel) | 4.4 | N/mm | ASTM D3330 |
| Chemical Resistance - Cleavage Peel (3 Days at RT) | 12.3 | N/mm | FLTM BU 112-02, Method C |
| Chemical Resistance - Cleavage Peel (Unleaded Gasoline - 1hr) | 11.4 | N/mm | FLTM BU 112-02, Method C |
| Chemical Resistance - Cleavage Peel (Diesel Fuel - 1hr) | 10.5 | N/mm | FLTM BU 112-02, Method C |
| Chemical Resistance - Cleavage Peel (Water Immersion - 240hrs) | 11.4 | N/mm | FLTM BU 112-02, Method C |
| UV Resistance (2 weeks UV-A at 140°F Initial strength) | min 90 | % | — |
| Application Temperature Range | 10 - 38 | °C | — |
| Service Temperature Range | -34 to 93 | °C | — |
Regulatory & Compliance
- Regulatory Information
Meets requirements of: Ford WSB-M3G138-B
Storage & Handling
- Shelf Life
- 24 months
- Storage and Shelf Life Conditions
Store material in original unopened packaging at temperatures between 4°C to 38°C (40°F to 100°F). Shelf life is 24 months when stored as recommended.