H.B. Fuller MP5405FLEXMV
1 of 79 products in this brandH.B. Fuller MP5405FLEXMV is a two-part unfilled rubber modified medium viscosity epoxy adhesive designed for high-speed bonding of metals, ceramics, and most plastics. It cures to a tough, semi-rigid material that is free-flowing in viscosity. It has good resistance to water, salt spray, inorganic acids and bases, and most organic solvents. It was specially formulated to a 1:1 mix ratio for use in either MMD equipment or side-by-side dual cartridges for easy dispensing. A handling cure is normally achieved at room temperature within 20 - 30 minutes, with full cure in 24 hours. An elevated temperature cure schedule can be used to reach final properties quickly.
Chemical Family: Epoxy & Epoxy Derivatives
RTU Product Type: 2K (2 component) Adhesive, Epoxy Adhesive, Reactive Adhesive, Structural Adhesive
Application Area: Cartridge
Compatible Substrates & Surfaces: Ceramic, Composites, Elastomers & Rubbers, Glass, Metal, Plastics, Wood
Features: Excellent Salt Spray Resistance, Free Flowing, Good Adhesion, Good Toughness, Medium Viscosity, Room Temperature Curing, Solvent Resistance
Enhanced TDS
Identification
- Chemical Family
- GBU
- RTU Product Type
- Categories
-
Applications
- Application Area
- Compatible Substrates & Surfaces
Applications & Uses
- General Instructions
-
- Surfaces to be bonded must be clean, dry and free of other contaminants.
- Bring both components to room temperature prior to mixing.
- Measure out specified amounts of parts A and B and stir (without introducing bubbles) until homogenous or use a static mixing nozzle.
- Apply the uniform mixture to both surfaces.
- Allow to cure while being held in place with light clamping.
Features
- Ready-to-Use Product Features
Packaging & Availability
- Regional Availability
Physical Properties
- Color (Properties)
- Physical Form
- Appearance
-
Clear liquid
Properties
- Dielectric Strength:
-
16.1 kV/mm
- Strain at Break:
-
5~10 %
- Tensile Strength:
-
45.5 MPa
- Viscosity:
-
15000 cps
- Cured Properties
-
Value Units Test Method / Conditions Dielectric Constant (at 100Hz) 4.5 - ASTM D150 Dielectric Strength 16.1 kV/mm ASTM D149 Elongation at Break 5 - 10 % ASTM D638 Hardness 79 Shore D ASTM D2240 Operating Temperature - 40 to 130 °C - Tensile Strength 45.5 MPa ASTM D638 - Uncured Properties
-
Value Units Test Method / Conditions Handling Time Full Cure (at 23°C) 20 - 30 minutes - Handling Time Full Cure (at 66°C) 24 hours - Mix Ratio (by volume) 1:1 - - Pot Life (20 gram) 3 - 5 minutes - Specific Gravity (mix) 1.13 - - Specific Gravity (part A) 1.11 - - Specific Gravity (part B) 1.15 - - - Typical Properties
-
Value Units Test Method / Conditions Storage Temperature 12 - 25 °C - - Component B
-
Value Units Test Method / Conditions Viscosity (at 25°C) 15000 cPs - - Rheological Properties
-
Value Units Test Method / Conditions Viscosity (at 25°C) Paste - - - Component A
-
Value Units Test Method / Conditions Viscosity (at 25°C) Paste - - - Appearance
-
Clear liquid
Storage & Handling
- Storage Conditions
-
- Product should be stored in a cool and dry place out of direct sunlight.
- The shelf life is from date of manufacture.
- Shelf life is based on the products being stored properly at temperatures between 12°C and 25°C.
- Exposure to temperatures above 25°C will reduce the shelf life.
- This product should not be frozen.
- Shelf Life
-
12 months