H.B. Fuller EV Seal 200
1 of 44 products in this brandH.B. Fuller EV Seal 200 is an MS polymer system that can be used for 1K moisture curing or a 2K accelerated cure option. Fast skin-over and green strength at room temperature. The product shows superb mechanical properties and provides unparalleled levels of sealing and resistance. Suitable for adhesion to a wide range of substrates like plastics, metals, and composite materials.
RTU Product Type: 1K (1 component) Adhesive, 1K (1 component) Sealant, 2K (2 component) Adhesive, 2K (2 component) Sealant
Application Area: Battery Packs, Electric Vehicle (EV)
Compatible Substrates & Surfaces: Composites, Metal, Plastics
Features: Chemical Resistant, CTE Absorption, Excellent Substrate Adhesion, Fast Cure, Good Green Strength, Good Mechanical Properties, Good Weather Fastness, High Elasticity, High Elongation, High Strength, Moisture Resistant, Shock Absorbent, Thixotropic, Vibration Resistance, Wide Temperature Operating Range
Enhanced TDS
Identification
- GBU
- RTU Product Type
Application Information
- Cure Method
Applications
- Application Area
- Compatible Substrates & Surfaces
Features
- Ready-to-Use Product Features
-
Features & Benefits
- Labeling Claims
- Key Attributes
-
- Excellent sealing capability against weathering, moisture, and other external influences
- Wide temperature range
- Superb adhesion across wide substrate range
Identification & Functionality
- Product Information
-
Technology/Base MS Polymer Type of Product Elastic high strength adhesive/sealant Components 1K or 2K Curing Moisture Consistency Thixotropic
Packaging & Availability
- Packaging Type
- Regional Availability
- Typical Packaging
-
- 310 mL Cartridge
- 600 mL Sausage
- 25 kg pails
- 270 kg drums
Physical Properties
- Color (Properties)
Properties
- Density:
-
1400 kg/m³
- Solid Content:
-
100 %
- Specific Gravity:
-
1.4
- Tear Strength:
-
21 kN/m
- Tensile Strength:
-
3.2 MPa
- Uncured Properties
-
Value Units Test Method / Conditions Change in Volume -3 % DIN EN ISO 10563 Curing to Depth (within first 24 h) 3 mm/d Climate according to DIN 50014 Skin Formation Time 10 minutes Kö-test method 100109, DIN 50014 - Physical Properties
-
Value Units Test Method / Conditions Density 1.4 g/cm³ - Service Temperature (30 min) -60 to 90 °C - Short-Term Temperature Resistance (30 min) 200 °C - Solid Content 100 Wt(%) - Specific Volume Resistance min. 10000000000 ohm-cm Kö-test method 100262 - Cured Properties
-
Value Units Test Method / Conditions Elongation at Break 400 % DIN EN ISO 527 Hardness (after 28 days, thickness of specimen = 6 mm) 55 Shore A - Lap Shear Strength (aluminum) 3.5 MPa DIN EN 1465 Tear Strength 21 N/mm ASTM D624 Tensile Strength 3.2 MPa DIN EN ISO 527 Young's Modulus (at 100% elongation) 2 MPa DIN EN ISO 527, DIN 53 504 - Processing Parameters
-
Value Units Test Method / Conditions Processing Temperature 5 - 35 °C - Recommended Minimum Layer Thickness 2 mm - Required Squeezing Pressure 4 - 5 bar - Storage Temperature 5 - 25 °C -
Storage & Handling
- Storage & Handling Information
-
- EV Seal 200 should be used within the shelf life specified on the packaging. The storage stability only applies to material stored under appropriate conditions (original unopened containers, recommended storage temperature)
- Clean tools immediately after use. Once cured, the material can only be removed mechanically. Appropriate cleaners are listed in the product properties table. For further information please contact your local sales office.