H.B. Fuller 1527

Identification

GBU

EA

RTU Product Type

Encapsulant,

1K (1 component) Sealant,

1K (1 component) Adhesive,

Reactive Sealant,

Reactive Adhesive

Categories

Markets → Industrial → Applications → Renewable Energy → Energy Storage Systems

Markets → Industrial → Applications → Renewable Energy → Solar Energy

Markets → Industrial → Applications → Renewable Energy → Wind Energy

Technologies → Adhesives & Sealants → Product Families → Bonding Technology → 1K Liquid Reactive Adhesives

Technologies → Adhesives & Sealants → Product Families → Sealing Technology → Reactive Sealants

Application Information

Cure Method

Moisture Cure

Applications

Application Area

Photovolatics,

Solar Cell,

Electronic Components,

Turbines,

Edge Gluing,

Electrical Boxes,

Junction Boxes,

Solar Panel,

PV Modules,

Frame Sealing,

Blades,

Ingot Bonding,

Lithium-Ion Battery,

Energy Storage,

Module Installation,

Rail Bonding

Applications & Uses

Curing Conditions

Cure speed will vary with temperature, relative humidity, depth of material and presence of moisture. Some applications may require special surface preparation. At 21 -25°C, 45 - 55% relative humidity, typical cure depth is 2mm in 24 hours. Requires more time to cure in colder or lower humidity conditions.

General Instructions

• For best performance bond surfaces should be clean, dry and free of any contaminants and oils.
• Apply a continuous and even bead of silicone to one surface.
• Assemble parts immediately. Remove excess material at once.

Features

Ready-to-Use Product Features

Excellent Performance,

Good Weather Stability,

High Performance,

UV Resistant,

Enhanced Damp Proofing,

High Insulation Properties

Packaging & Availability

Regional Availability

• Asia Pacific
• Europe
• North America
• Latin America
• India/MiddleEast/Africa (IMEA)

Packaging Information

• 310ml
• 400ml
• 600ml
• 25kg
• 235kg

Physical Properties

Color (Properties)

Black,

White

Physical Form

Paste

Properties

Density:

1370 kg/m³

Specific Gravity:

1.37

Strain at Break:

300 %

Tensile Strength:

2.3 MPa

Cured Properties

	Value	Units	Test Method / Conditions
Elongation at Break	300	%	ISO37, GB/528
Hardness	48	Shore A	ISO7619, GB/T531
Lap Joint Shear Strength (aluminum)	1.8	MPa	ISO4587, GB7124
Tensile Strength	2.3	MPa	ISO37, GB/528
Thermal Service Range	- 54 to 210	°C	-

Typical Properties

	Value	Units	Test Method / Conditions
Performance Temperature	-54 to 210	°C	-
Storage Temperature	8 - 25	°C	-

Electrical Properties

	Value	Units	Test Method / Conditions
Breakdown Voltage	20	kV/mm	IEC 60243-1, GB/T1695
Volume Resistivity	1000000000000000	Ω-cm	IEC60093, GB/T1692

Technical Data

	Value	Units	Test Method / Conditions
Specific Gravity	1.37	-	-

Damp Heat Aging Test Properties

	Value	Units	Test Method / Conditions
Elongation at Break (at 85ºC, 85% relative humidity for 1000h)	320	%	ISO37, GB/528
Tensile Strength (at 85°C, 85%RH, 1000h)	1.6	MPa	ISO37, GB/528

Uncured Properties

	Value	Units	Test Method / Conditions
Full Cure Time (at 21 - 25°C, 45 - 55% relative humidity, min. 2mm, full uncured)	24	hours	-
Tack Free Time	6	minutes	-

Regulatory & Compliance

Certifications & Compliance

UL Certified

Storage & Handling

Storage Condition

Product shall be ideally store in a cool, dry area in unopened containers. Material should be stored at a temperature of 8 - 25°C.

Shelf Life

12 months