H.B. Fuller

Identification

Chemical Family: Polyurethanes (PU)
GBU: BAS
RTU Product Type: Hot Melt Adhesive,

Reactive Adhesive

Categories: Markets → Building & Construction → Applications → Building Materials → Interior Fixtures

Markets → Building & Construction → Applications → Building Materials → Wood

Markets → Building & Construction → Applications → Decorative Materials & Finishes → Wallcoverings & Decorative Laminates

Markets → Consumer Goods → Applications → Furniture

Technologies → Adhesives & Sealants → Product Families → Bonding Technology → Hot Melt Reactive Adhesives

Applications

Application Area: Decorative Surfaces,

Furniture,

Doors,

Door Frames,

Veneering,

Woodwork,

Flat Lamination,

Lamination,

Engineered Wood Flooring,

Wooden Surfaces,

Rigid Foam
Application Method: Roller,

Spray,

Nozzle
Compatible Substrates & Surfaces: Metal,

Paper,

Plastics,

Textiles,

Wood,

Composites,

Polycarbonate (PC),

Acrylonitrile Butadiene Styrene (ABS),

Polyvinyl Chloride (PVC),

Expanded Polystyrene (EPS),

Foils,

Extruded Polystyrene (XPS)

Applications & Uses

Processing Information

Lower temperatures than recommended can cause higher viscosity which result in reduced bond strength and reduced wetting. Refer to the technical data table regarding processing parameters. Lower temperatures than recommended can cause higher viscosity which result in reduced bond strength and reduced wetting. Depending on the construction of the equipment, a continuous heating above processing temperature can cause decomposition of the adhesive. Tank melters should use protective gases with < 5 ppm humidity, only. Rakoll® 5010 is moisture sensitive, therefore container must be kept closed.

Recommended Conditions

Recommended Conditions for Good Results

Ambient Temperature	18°C to 20°C
Substrate Temperature	18°C to 20°C
Adhesive Temperature	18°C to 20°C
Moisture Content of Wood	8% - 10%
Relative Humidity	40% - 60%

Features

Ready-to-Use Product Features: Excellent Strength,

Good Adhesion,

Good Bonding Strength,

Good Mechanical Properties,

Good Thermal Stability,

Highly Versatile,

Very Good Heat Resistance,

Long Open Time

Features & Benefits

Labeling Claims

Sustainable,

Non-Hazardous

Product Benefits

High thermal stability after complete cross-linking
Good adhesion to various plastic substrates
High heat resistance
Low content of monomeric MDI (<0,1%)
High mechanical properties
High initial bonding strength
Long open time

Packaging & Availability

Regional Availability

Europe
India/MiddleEast/Africa (IMEA)

Properties

Typical Properties


	Value	Units	Test Method / Conditions
Application Temperature	120 - 140	°C	-
Density	1.2	g/cm³	-
Open Time	max. 6	m	-
Viscosity (at 120°C)	14500	mPa.s	-

Processing Properties


	Value	Units	Test Method / Conditions
Curing Time (for Final Properties) (at 20°C, 65 % RH, depending on ambient temperature and relative air humidity)	3 - 4	d	-
Open Time (depending on temperature, coating weight and substrate)	6	min	Internal HBF Standard
Processing Temperature	120 - 140	°C	-
Storage Temperature	- 25 to 35	°C	-
Viscosity (at 130 °C, Sp. 29, 20 rpm)	15000	mPa·s	Brookfield Thermosel

Storage & Handling

Storage Information: Rakoll® 5010 should be used within the shelf life specified on the packaging. The storage stability applies to material stored under appropriate conditions only (original unopened containers, recommended storage temperature).

Technical Details & Test Data