H.B. Fuller

Applications & Uses

Application Information

Applications	Fields of Application	Automotive
		Construction
		Industrial assembly
		Transportation
Processing	Suitable Substrates	Various galvanized steels
		Various aluminum alloys
		Various steel alloys
		Duroplastics
		Thermoplastics (except PE, PP, PTFE)
		Glass
		Mineralic materials
		Wood
	Consistency	Non-sagging Pasty
	Surface Requirements	Clean
		Free of grease
		Free of dust
	Surface Cleaning	Körasolv GL
		Körasolv PU
		Körasolv WL
	Adhesion Promoter (absorbing surface)	Körabond HG 74 E
	Adhesion Promoter (non absorbing surface)	Körabond HG 83
	Application Method	Cartridge dispenser
	Product is free of	Solvents
Cleaning	Cleaner for Tools	Körasolv GL
Cleaning	Cleaner for Tools	Körasolv PU
Hints	Resistance against UV Radiation	Not suitable for glass bonding with permanent UV radiation to the bonding area. Please ask your local sales office for products suitable for such applications
	Stress Cracking	Preliminary tests must be carried out on plastics with a tendency to stress cracking. (PMMA, ABS, PC or PS)
	Compatibility with Polystyrene Foams	Not suitable for bonding polystyrene foams. Please ask your local sales office for products suitable for such applications.

Cleaning Instructions

Clean tools immediately after use. Once cured, the material can only be removed mechanically. Appropriate cleaners are listed in the product properties.

Dimensioning

The required thickness of the adhesive layer depends on the expected maximum strength and joint movement. We recommend a minimum layer thickness of 2 mm.

Preparation

For some substrates the use of mechanical pretreatment and/or cleaner or primer is necessary to achieve good adhesion.

Processing

Low temperatures can cause a temporary increase in viscosity resulting in reduced extrusion and slower curing rates.

Features

Ready-to-Use Product Features: Excellent Elasticity,

Excellent Moisture Resistance,

Excellent Strength,

Good Adhesion,

Good Flexibility,

Good Sagging Resistance,

Good Weather Stability,

High Flexibility,

UV Resistant,

Improved Ageing Resistance,

Good Cold Resistance

Packaging & Availability

Country Availability

Australia,

Canada,

Switzerland,

China (Mainland),

Japan,

Korea,

Malaysia,

New Zealand,

Philippines,

Turkey,

Taiwan,

USA

Regional Availability

Asia Pacific
Europe
North America

Physical Properties

Physical Form: Paste

Properties

Density:

1060 kg/m³

Solid Content:

100 %

Specific Gravity:

1.06

Strain at Break:

300 %

Tensile Strength:

3 MPa

Note

¹ - Climate according to DIN 50 014
² - within first 24 h; Climate according to DIN 50 014
³ - after 28 d; thickness of specimen = 6 mm

Physical Properties


	Value	Units	Test Method / Conditions
Density	1.06	g/cm³	DIN 53479
Loss on Weight (after 14 days)	1.0	%	-
Solid Content	100.0	wt %	-

Cured Properties


	Value	Units	Test Method / Conditions
Curing to Depth (within first 24 h)²	3.0	mm/d	-
Elongation at Break	300.0	%	DIN EN ISO 527
Hardness	40.0	-	ISO 868/DIN 53 505, Shore A
Skin Formation Time¹	10.0	min	Kö-test method 100109
Tensile Strength	3.0	MPa	DIN EN ISO 527

Recommended Operating Conditions


	Value	Units	Test Method / Conditions
Service Temperature	-60 to 90	°C	-
Short-Term Temperature Resistance (30 min)	120.0	°C	-

Processing Parameters


	Value	Units	Test Method / Conditions
Processing Temperature	5 - 30	°C	-
Recommended Minimum Layer Thickness	2.0	mm	-

Storage & Handling

Storage Conditions: Körapop should be used within the shelf life specified on the packaging. The storage stability only applies to material stored in original unopened containers, at storage temperature 5°C to 25°C.

Körapop Transparent

Enhanced TDS