Cyberbond 5005

Identification

Chemical Family

Cyanoacrylates

GBU

HHC

RTU Product Type

Anaerobic Adhesive,

1K (1 component) Adhesive

Categories

Markets → Automotive & Transportation → Applications → Automotive → Interior

Markets → Consumer Goods → Applications → Appliances & Electronics

Markets → Healthcare & Pharma → Applications → Medical → Medical Devices & Assemblies

Technologies → Adhesives & Sealants → Product Families → Bonding Technology → Anaerobic Adhesives

Application Information

Cure Method

Moisture Cure

Applications

Application Area

Medical Devices

Segment

Medical

Applications & Uses

General Instructions

Surfaces to be bonded should be clean and dry. Dispense a drop or drops to one surface only. Apply only enough to leave a thin film layer after compression. Press parts together and hold firmly for a few seconds. Good contact is essential. An adequate bond develops in less that one minute and maximum strength is attained in 24 hours. Wipe off excess adhesive from the top of the container and recap. products if left uncapped may deteriorate by contamination from moisture in the air. Because products cure by polymerization, whitening may appear on the surface of the container or the bonded materials. This will not affect adhesive performance.

Features

Ready-to-Use Product Features

Excellent Part Finish (Low Bloom),

Low Blooming,

Low Odor,

Low Viscosity,

Solvent Resistance

Packaging & Availability

Country Availability

India

Regional Availability

• Asia Pacific
• Europe
• North America
• Latin America
• India/MiddleEast/Africa (IMEA)

Physical Properties

Physical Form

Liquid

Properties

Density:

1060 kg/m³

Flash Point:

80 °C

Shear Strength:

17.914 MPa

Specific Gravity:

1.06

Viscosity:

2~6 cps

Note

*** Performance of cured adhesive on Stainless Steel

Cured Properties

	Value	Units	Test Method / Conditions
Cure Time (full)	24	hours	-
Service Temperature Range	- 55 to 95	°C	-

Typical Properties

	Value	Units	Test Method / Conditions
Fixture Time	15	seconds	-
Shear Strength***	2600	psi	-
Storage Temperature	15.5 - 25	°C	-
Temperature Range	-67 to 203	°F	-

Technical Data

	Value	Units	Test Method / Conditions
Specific Gravity	1.06	-	-

Uncured Properties

	Value	Units	Test Method / Conditions
Flash Point	80	°C	-
Set Time (Acrylonitrile Butadiene Styrene)	10	seconds	-
Set Time (Ethylene Propylene Diene Monomer)	5	seconds	-
Set Time (steel, uncured)	15	seconds	-

Performance Properties

	Value	Units	Test Method / Conditions
Pressure (performance of cured adhesive, ABS)	580 - 765	psi	ASTM 4501
Pressure (performance of cured adhesive, PC)	940 - 1250	psi	ASTM 4501
Pressure (performance of cured adhesive, PVC)	485 - 1055	psi	ASTM 4501
Pressure (performance of cured adhesive, aluminum)	2020 - 2240	psi	ASTM 4501
Pressure (performance of cured adhesive, steel)	1600 - 2920	psi	ASTM 4501

Rheological Properties

	Value	Units	Test Method / Conditions
Viscosity (at 20 - 25°C)	2 - 6	cPs	Brookfield SC4-21

Regulatory & Compliance

Certifications & Compliance

ISO 10993,

ISO 13485

Storage & Handling

Storage Conditions

Containers should be stored in a cool, dry, dark area. Storage temperature 15.5°C - 25°C (60°F - 77°F), without exposure to direct light or heat. Do not refrigerate.

Shelf Life

12 months (uncured)

Technical Details & Test Data

Curing Performance

Ambient surface moisture initiates the curing process. Handling strength is reached in a short time, and will vary based on environmental conditions, bond line gap, and other factors. Product will continue to cure for at least 24 hours before full strength and solvent resistance is developed.

Heat Aging (aged at temperature indicated and tested at 22°C)

Hot Strength (%RT strength, tested at temperature)

Performance Range by Substrate (N/mm²)

Performance of Cured Adhesive

Substrate	N/mm²	PSI
Steel	11.0 to 20.1	1600 to 2920
AL	13.9 to 15.4	2020 to 2240
PC**	6.5 to 8.6	940 to 1250
PVC**	3.3 to 7.3	485 to 1055
ABS**	4.0 to 5.3	580 to 765

 

*Rubber figures given are typical. Your results may vary by specific rubber type.
**Tested to ASTM 4501
***n/r = not recommended

Solvent Resistance

Solvent	Example	Resistance
Alcohol	Ethanol, Methanol	+ + +
Ester (aromatic)	Ethylacetate	+ + +
Ketone (aromatic)	Acetone, Benzophenone	– – –
Aliphatic hydrocarbon (alkanes)	Petrol, Heptanes, Hexane	+ + –
Aromatic hydrocarbons	Benzyl, Toluol, Xylol	+ + –
Halogenated hydrocarbons	Methylenchloride, Chloroform, Chlorobenzol	– – –
Weak aqueous	Nitrite, muriatic acid, sulphuric acid, phosphoric acid	+ + + (– – – if concentrated)
Weak aqueous base	sodium hydroxide solution, caustic potash	+ + + (– – – if concentrated)

Time Until Full Cure (% of RT strength)