Cyberbond CB AT 1735
1 of 68 products in this brandRTU Product Type: 2K (2 component) Adhesive, Reactive Adhesive
Application Area: Joints
Compatible Substrates & Surfaces: Acrylonitrile Butadiene Styrene (ABS), Composites, Metal, Plastics, Polyamide, Polycarbonate (PC), Poly(Methyl Methacrylate) (PMMA), Polyvinyl Chloride (PVC)
Chemical Family: Acrylics, Acrylates & Methacrylates
Features: Fast Cure, General Purpose, Good Adhesion, High Flexibility, Long Open Time, Thixotropic, Weak Acid Resistant, Weak Base Resistant
-
Type Document Name
-
Technical Data SheetCyberbond CB AT 1735 Technical Data Sheet
Enhanced TDS
Identification
- Chemical Family
- GBU
- RTU Product Type
- Categories
Applications
- Application Area
- Compatible Substrates & Surfaces
Applications & Uses
- Clean Surface
-
Surfaces should be clean, dry and free of grease before bonding.
Features
- Ready-to-Use Product Features
Features & Benefits
- General Information about MMA adhesives
-
2-component methacrylate adhesives belong to the group of reactive adhesives. The reaction starts by mixing hardener and resin. Cyberbond offers these adhesives in double cartridges in 1:1 or 10:1 ratio with static mixing tubes. This allows an easy and quick application. Methacrylate adhesives are available in different viscosities from liquid to paste-like and with different curing times. They are characterized by excellent adhesion to metals, many plastics and composite materials. The mechanical properties range from flexible to rigid.
Identification & Functionality
- Base Compound (Liquid State)
-
Methyl methacrylate
Packaging & Availability
- Packaging Type
- Regional Availability
Properties
- Application Temperature:
-
-50~120 °C
- Density:
-
1070 kg/m³
- Flash Point:
-
10 °C
- Shelf Life:
-
12 months
- Specific Gravity:
-
1.07
- Tensile Modulus:
-
400~600 MPa
- Tensile Strength:
-
12~16 MPa
- Viscosity:
-
10.000~25.000 cps
- Physical Properties
-
Value Units Test Method / Conditions Cure Time (full, polymer) 24 hours - E-Modulus (polymer) 400 - 600 MPa - Elongation at Break (polymer) 150 - 200 % - Fixture Time (liquid state) 20 - 40 minutes - Flash Point (liquid state) 10 °C - Mix Ratio (liquid state) 1:1 - - Open Time (liquid state) 15 - 20 minutes - Temperature Range (polymer) -50 to 120 °C - Tensile Strength (polymer) 12 - 16 MPa - Viscosity (at 20°C, 0.5 s⁻¹) 80000 - 140000 mPa.s Cone-Plate Viscometer Viscosity (at 20°C, 160 s⁻¹) 10000 - 25000 mPa.s Cone-Plate Viscometer - Typical Properties
-
Value Units Test Method / Conditions Set Time 20 - 40 minutes - Storage Temperature 10 - 20 °C -
Regulatory & Compliance
- Certifications & Compliance
Storage & Handling
- Storage Conditions
-
Store products in a cold and dark place at temperatures between 10°C to 20°C.
- Shelf Life
-
12 months
Technical Details & Test Data
- Property Details & Graph
-
Adhesive performance Tensile shear strength
Substrate, Result N/mm² Tensile shear strength (Polycarbonate,Fail) 6 - 10 Tensile shear strength (PMMA, Fail) 8 - 12 Tensile shear strength (ABS, Fail) 8 - 12 Tensile shear strength (PVC, Fail) 8 - 12 Tensile shear strength (Stainless steel) 23 - 26 Tensile shear strength (Aluminum) 16 - 22 Tensile shear strength
Hot strength tested at temperature
Resistance against solvents
Solvent Resistance Weak acids very good Weak bases very good Polar solvents limited Strong acids and bases limited Measurement of Viscosity
Viscosity describes the flow-ability of a liquid. Cyberbond measures the viscosity of the products by means of the cone/plate method: the liquid is applied on a panel and a defined cone presses the liquid together and rotates. Newtonian fluids are measured at shear rate 160 s-1, thixotropic products are measured at shear rate 0,5 s-1 and 160 s-1. The viscosity is measured in mPa*s at 20 °C.